Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Modulus | 143 GPa | 20700 ksi | Calculated |
Sapco 95% Aluminum Oxide Information provided by Sapco. |
|||
Shear Modulus | 143 GPa | 20700 ksi | Calculated |
Sapco 98% Aluminum Oxide Information provided by Sapco. |
|||
Shear Modulus | 143 GPa | 20700 ksi | Calculated |
CoorsTek CAP 4 98.5% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
Shear Modulus | 143 GPa | 20700 ksi | Calculated |
CoorsTek FG-98 98% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
Shear Modulus | 143 GPa | 20700 ksi | Calculated |
CoorsTek FG-995 Alumina (nom. 98.5% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Shear Modulus | 143 GPa | 20700 ksi | Calculated |
CeramTec Rubalit® A 1898 Alumina, 98% Rubalit® A 1898 (98%) was specifically developed in response to electrical and electronic engineering needs. In conjunction with CeramTec's complementary metallization systems, a vacuum-tight bond .. |