Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® BFL4000U PC (Asia Pacific) Lexan* BFL4000U Polycarbonate resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating and good impact/flow balance. Designed fo.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® BFL4000U PC (Europe-Africa-Middle East) Lexan* BFL4000U Polycarbonate resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating and good impact/flow balance. Designed fo.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Custom Resins Vexel™ 3250 PBT
(discontinued **) General Purpose Unreinforced; High Flow. Property data for dry as molded samples.Data provided by the manufacturer |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Ensinger ENSITEP® PBT Polybutylene Terephthalate - Extruded Products
(discontinued **) ENSITEP BT is an unreinforced thermoplastic polyester derived from polybutylene terephthalate. Its excellent wear and impact resistance, low coefficient of friction, high flexural modulus, and supe.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Ineos Nova 1210 High Heat Crystal Polystyrene
(discontinued **) High heat resistance, High molecular weight, optimum performance in extruded foamApplications: Meat and poultry trays, Egg cartons, Food packagingExposure to gamma radiation in the 2.02-6.06 megarad.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Ineos Nova 1230 High Heat Crystal Polystyrene
(discontinued **) Good processing characteristics, Low residual monomer, Low oligomersApplications: Direct injection foam, Biaxially oriented sheet, Glazing sheetExposure to gamma radiation in the 2.02-6.06 megarad r.. |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Plenco 4100 Phenolic, Granular, Compression Molded
(discontinued **) Two-stage Phenolic. PLENCO 04100 is a black two stage, medium heat resistant phenolic molding compound. It has excellent moldability characteristics and molded finish. It is used in appliance and .. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Plenco 309 Black (COM) Mineral/Fiber Filled Phenolic Molding Compound
(discontinued **) Plaslok 309 is a two-stage, mineral and fiber-filled phenolic molding compound having excellent impact strength; and as such, is considered a good candidate for replacing chopped-fiber filled compou.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC LNP* Lubricomp* Lexan_WR5210R compound is a wear resistant, 7% PTFE filled PC. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RL0039XP PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RL0039XP is a compound based on PA66 resin containing PTFE, Flame Retardant. Added features include ; Flame Retardant, internally Lubricated. |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Techmer ES Elastoblend® PA6/6 IM 408 L Nylon 66 Availability: North AmericaForms: PelletsAdditive: Lubricant and Impact ModifierFeatures: Lubricant and Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc... |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Techmer ES Elastoblend® PC E IM Availability: North AmericaForms: PelletsAdditive: Impact ModifierFeatures: Impact Modified and High ViscosityProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP WG003 PBT (Europe-Africa-Middle East) LNP* LUBRICOMP* WG003 is a compound based on Polybutylene Terephalate resin cantain Graphite. Added features include: Internally Lubricated. |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Spartech Royalite R71/920 PC/ABS Fire Rated Sheet Description: Fire Rated SheetInformation provided by Spartech. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Xylex X7300OQ PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. High flow with good impact and excellent optical quality.This data was supplied by SABIC-IP for the Europe-Africa-Middle East.. |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Techmer ES HiFill® POM HO UV Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: HomopolymerInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Techmer ES Plastiblend® PA6/6,6 IM 6040 BK MB Nylon 6/66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Copolymer, Impact Modified and LubricatedAppearance: BlackProcessing Metho.. |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Techmer ES Plastiblend® PC/ABS FR 6206 Availability: North AmericaForms: PelletsFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® DP 1-1456 Polycarbonate, Impact Grade Impact modified injection molding grade, extremely easy flow and easy mold release, for thin walled applications with long flow lengths.Information provided by Bayer.As of 1 September 2015, Bayer Ma.. |
|||
Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
Clariant Renol PA2SP0017 Nylon 6, Impact Modified Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboWeld 48-14/AboCure 48-14 Adhesive/Casting Resin Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 45-10/AboCure 45-10 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Ineos Nova 1220 High Heat Crystal Polystyrene
(discontinued **) Good processing characteristics, Low residual monomer, Low oligomersApplications: Direct injection foam, Biaxially oriented sheet, Glazing sheetExposure to gamma radiation in the 2.02-6.06 megarad r.. |
|||
Flexural Yield Strength | 83.0 - 207 MPa | 12000 - 30000 psi | Average value: 158 MPa Grade Count:21 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled". Each property range of values reported is .. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
PolyOne Lubri-Tech™ MP-15MCF/15T-2S Modified PPO - 15% Milled Carbon Fiber - 15% PTFE - 2% Silicone