Polymer Property : Flexural Yield Strength = 25700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 177 MPa
25700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East)
LNP* LUBRICOMP* DFL36E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features include; Internally Lubricated, Easy Molding.
Flexural Yield Strength 177 - 420 MPa
25700 - 60900 psi
Average value: 331 MPa Grade Count:45
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi..
Flexural Yield Strength 177 MPa
25700 psi
ASTM D790
Plenco 51240 PET, Pellet, Injection Molded, Black  (discontinued **)
PLENCO 51240 is an engineering grade glass reinforced flame retarded recycled polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed.Information supplied by P..
Flexural Yield Strength 177 MPa
25700 psi
DIN 53452; ASTM D790
Kolon Kopa® KN163G30 Nylon 6 Resin
KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c..
Flexural Yield Strength 177 MPa
25700 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT
LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare.
Flexural Yield Strength 177 MPa
25700 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66
LNP* STAT-KON* RFD03 is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material is: Electrically Conductive.
Flexural Yield Strength 177 MPa
25700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP JF004ER PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF-1004 S-3 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release.
Flexural Yield Strength 177 MPa
25700 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® SHF4960 PBT (Europe-Africa-Middle East)
Valox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release.
Flexural Yield Strength 177 MPa
25700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP LX97024 PEEK (Europe-Africa-Middle East)
LNP* LUBRICOMP* LX97024 is a compound based on Polyetheretherketone containing Glass Fiber, PTFE. Added features include: Internally Lubricated, Easy Molding.
Flexural Yield Strength 177 MPa
25700 psi
ASTM D790
Toyobo Vylopet® EMC130-04 Glass Reinforced Polyester, Easy Molding Grade
Key Feature: Flame retardant V-0 UL-94 classApplications: General componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking r..
Flexural Yield Strength 177 MPa
25700 psi
ASTM D790
Toyobo Vylopet® EMC430 PET/PBT Blend
Key Feature: HB UL-94 ClassApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical pro..
Flexural Yield Strength 177 MPa
25700 psi
ASTM D790
Solvay Specialty Polymers Amodel® AF-1550 V0 Polyphthalamide (PPA) Resin, 50% Glass/Mineral Reinforced, at 50% RH &
Data provided by the manufacturer, Amoco Corporation.AMODEL AF-1550 V0 resin is a 50% glass/mineral reinforced, flame retarded polyphthalamide (PPA) that features: high deflection temperature, high ..