Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 309 MPa | 44800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP UX06427 PPA LNP* LUBRICOMP* UX06427 is a compound based on PPA containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include: Heat Stabilized, Hot Water Moldable, Wear Resistant. |
|||
Flexural Yield Strength | 309 MPa | 44800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP PX94085 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PX94085 is a compound based on PA6 resin, containing Glass Fiber. |
|||
Flexural Yield Strength | 309 MPa | 44800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP VERTON PX06418 PA 6 LNP* VERTON* PX06418 is a compound based on Nylon 6 containing proprietary fillers. Added features of this grade are: Heat Stabilized, Structural. |