- SABIC Innovative Plastics LNP LUBRICOMP UX06427 PPA
SABIC Innovative Plastics LNP LUBRICOMP UX06427 PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UX06427 PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* UX06427 is a compound based on PPA containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include: Heat Stabilized, Hot Water Moldable, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.600 % | 0.600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00060 - 0.00090 cm/cm @Time 86400 sec |
0.00060 - 0.00090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm @Time 86400 sec |
0.0060 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 224 MPa | 32500 psi | Type I, 5 mm/min; ASTM D638 |
| 227 MPa | 32900 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 224 MPa | 32500 psi | Type I, 5 mm/min; ASTM D638 |
| 227 MPa | 32900 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 |
| 1.3 % | 1.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 |
| 1.3 % | 1.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 22.77 GPa | 3303 ksi | 1 mm/min; ISO 527 |
| 25.2 GPa | 3650 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 311 MPa | 45100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 309 MPa | 44800 psi | 2 mm/min; ISO 178 |
| 311 MPa | 45100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 17.2 GPa | 2490 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 19.64 GPa | 2849 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.46 J/cm | 12.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.33 | 0.33 | ASTM D3702 Modified |
| K (wear) Factor | 52.4 x 10-8 mm³/N-M | 26.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 34.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 298 °C | 568 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 296 °C @Thickness 3.20 mm |
565 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 284 °C | 543 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 284 °C @Thickness 3.20 mm |
543 °F @Thickness 0.126 in |
unannealed; ASTM D648 |