Polymer Property : Flexural Yield Strength = 42100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	290 MPa	42100 psi	ASTM Data
BASF Capron® GR30 30% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron GR30 is a 30% glass reinforced polyamide 6 injection molding compound. IT is also available in heat stabilized (Capron GR30 HS) and/or pigmented versions. The glass fiber reinforcement enhanc..
Flexural Yield Strength	290 MPa	42100 psi	ASTM Data
BASF Capron® SEG7 35% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron SEG7 is an unfilled injection molding type 6 nylon graft copolymer. It has superior impact resistance and flow especially for thinner walled parts and long flow lengths. Copolymerization res..
Flexural Yield Strength	290 - 450 MPa	42100 - 65300 psi	Average value: 389 MPa Grade Count:9
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl..
Flexural Yield Strength	290 - 290 MPa @Temperature 80.0 - 80.0 °C	42100 - 42100 psi @Temperature 176 - 176 °F	Average value: 290 MPa Grade Count:2
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl..
Flexural Yield Strength	290 MPa	42100 psi	ASTM D790
Solvay Specialty Polymers AmodelÂ® AS-1566 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) AmodelÂ® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifica..
Flexural Yield Strength	290 MPa	42100 psi	ASTM D790
Solvay Specialty Polymers AmodelÂ® AS-4133 L Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications ..
Flexural Yield Strength	290 MPa	42100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP QC006 PA6.10 (Europe-Africa-Middle East) LNP * THERMOCOMP* QC006 is a compound based on PA610 resin containing Carbon Fiber. Added features include; Electrically Conductive.
Flexural Yield Strength	290 MPa	42100 psi	ASTM D790
E-Polymers TEKAMID® TA210G33 , 33% Glass Fiber Reinforced PA66, DAM 33% Glass Fiber reinforced, High strengthInformation provided by E-Polymers Co. Ltd.
Flexural Yield Strength	290 MPa	42100 psi	ASTM Data
BASF Capron® GR30 HS 30% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron GR30 HS is a heat stabilized 30% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aest..
Flexural Yield Strength	290 MPa	42100 psi	ASTM D790
Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA) (Unverified Data**) Amodel AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications incl..
Flexural Yield Strength	290 MPa	42100 psi	ASTM D790
Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically ..