Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® C1000HF PC+ABS (Asia Pacific) High flow PC+ABS. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 923 PC (Asia Pacific) Opaque colors, low viscosity, superior flame retardance. Decreased smoke and lowered toxic gas emission. UV-stabilized. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 923ASR PC More robust design of standard 900 series flame retardant grade. Internal mold release. UV-stabilized. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 940ASR PC More robust design of standard 900 series flame retardant grade. Internal mold release. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 943A PC Medium viscosity, superior flame retardance. UV-Stabilized. Clear, tints and opaque colors. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 943AR PC (Asia Pacific) Medium viscosity, superior flame retardance. UV-Stabilized. Clear, tints and opaque colors. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 943ASR PC (Asia Pacific) More robust design of standard 900 series flame retardant grade. Internal mold release. UV-stabilized. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® HFD1830 PC Copolymer (Asia Pacific) 40 MFR LEXAN High Flow Ductile Copolymer UV Stabilized, available in transparent colors only |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® ML4506 PC Transparent polycarbonate for aircraft applications requiring FAR 25.853a compliance. Injection moldable. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DL001 is a compound based on Polycarbonate resin containing PTFE. Added features include: Internally Lubricated. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 920A PC (Asia Pacific) Low viscosity injection moldable, flame retardant PC. Exceptional surface appearance. Clear, tints and opaque colors. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 943A PC (Asia Pacific) Medium viscosity, superior flame retardance. UV-Stabilized. Clear, tints and opaque colors. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 9925A PC (Asia Pacific) Lexan 9925A is a flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance. It intended to meet WEEE/RoHS requireme.. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® EXL8414 PC Copolymer (Asia Pacific) Lexan* EXL8414 is a PC/siloxane copolymer resin with medium flow, excellent low temperature impact and 25% post consumer recycle content. Limited availability and restricted color only. Higher color.. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may af.. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® FXE9925A PC (Asia Pacific) Illuminate / edge glow color effect grade of Lexan 9925A. 9925A is a flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR .. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer (Europe-Africa-Middle East) 40 MFR LEXAN High Flow Ductile Copolymer |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® HFD1830 PC Copolymer (Europe-Africa-Middle East) 40 MFR LEXAN High Flow Ductile Copolymer UV Stabilized, available in transparent colors only |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RL004 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RL004 is a compound based on Nylon 66 resin containing PTFE. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Spartech Royalite R922 PC/ABS Aircraft Grade Sheet Description: Aircraft Grade SheetInformation provided by Spartech. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Techmer ES Plastiblend® PC/ABS 1950 Availability: North AmericaForms: PelletsInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Noryl PX0346 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Westlake Plastics Radel® R 5500 Polyphenylsulfone For Medical Applications Medical grade Radel R5500 resin offers exceptional hydrolytic stability, toughness, heat deflection temperature and resistance to stress cracking. This polymer also has excellent thermal stability,.. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 6485 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding grade with easy mold release, not available in transparent colors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was .. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 6555 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding with easy mold release, burning behavior.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG a.. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 940A PC (Asia Pacific) Medium viscosity, flame retardant PC. Exceptional surface. Clear, tints and opaque colors. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 953A PC Clear, tints and opaque colors, high viscosity, flame retardant with exceptional surface. UV-stabilized. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer 40 MFR LEXAN High Flow Ductile Copolymer |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 940 PC (Asia Pacific) Opaque colors, medium viscosity, superior flame retardance. |
|||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 950 PC (Asia Pacific) Opaque colors, high viscosity, superior flame retardance. |