Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
0.8 sec, LTS; ExxonMobl Method |
ExxonMobil Bicor™ 20MB668 OPP Film Product Description: Bicor 20MB668 is a high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS coating provid.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa |
410 g/in @Pressure 20.0 psi |
ESM, 0.8 sec, Untreated; ExxonMobl Method |
ExxonMobil Bicor™ 25ICT OPP Film Product Description: A one-side sealable, very broad seal range coextruded BOPP. This film is designed for use in unsupported plain or surface printed high-speed horizontal applications. The enhance.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.8 sec; ExxonMobl Method |
ExxonMobil Bicor™ 25MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low seal temperature (VLTS) coating. VLTS coating provides excellent perf.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.8 sec; ExxonMobil Method |
ExxonMobil Bicor™ 26MB768 OPP Film Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated on one side PVdC, one side very low temperature seal (VLTS) coating. PVdC provides an excellent moi.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.2 sec; ExxonMobil Method |
ExxonMobil Bicor™ 30MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side very low temperature seal (VLTS) coating. VLTS coating provides excellent performances on high s.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.2 sec; ExxonMobil Method |
ExxonMobil Bicor™ 32MB768 OPP Film Product Description: A High gas barrier, biaxially oriented transparent polypropylene film, coated on one side PVdC, one side very low temperature seal (VTLS) coating. PVdC provides excellent moistu.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.8 sec; ExxonMobil Method |
ExxonMobil Bicor™ 40MB668 OPP Film Product Description: A high speed transparent biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS coating provides excellent perfo.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C |
410 g/in @Pressure 40.0 psi, Temperature 266 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
ExxonMobil Metallyte™ 38MW480 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film, metalized on one side.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Outstanding opacity an.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.8 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 30MW648 OPP Film Product Description: A high speed super white opaque, biaxially oriented polypropylene film coated one side acrylic, one side very low temperature seal (VTLS) coating. VLTS coating provides an excel.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
410 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 35MD447 OPP Film Product Description: A coextruded super white opaque, modified high density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for use.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C |
410 g/in @Pressure 40.0 psi, Temperature 266 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 35MW647 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film acrylic coated two sides. Provides outstanding performances on all types of packaging machines.Availability: Africa & .. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C |
410 g/in @Pressure 40.0 psi, Temperature 266 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 38MO447 OPP Film Product Description: A coextruded white opaque, low density, biaxially oriented polypropylene film, heat sealable on the inside. The treated layer must be printed and varnished to provide the necess.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.8 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 40MW648 OPP Film Product Description: A high speed super white opaque, biaxially oriented polypropylene film coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS coating provides an excel.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
LTS, 0.8 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 42AH748 OPP Film Product Description: A high barrier, high speed, super white opaque, modified higher density biaxially oriented polypropylene film, coated one side high barrier PVdC, one side very low temperature s.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
0.8 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 42MH648 OPP Film Product Description: A high speed super white opaque, modified higher density, biaxially oriented polypropylene film, acrylic coated one side acrylic, one side very low temperature seal (VLTS) coati.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C |
410 g/in @Pressure 20.0 psi, Temperature 176 °F |
0.8 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 52MH648 OPP Film Product Description: A high speed super white opaque, modified higher density, biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
410 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 30MD447 OPP Film Product Description: A coextruded super white opaque, modified higher density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for u.. |
|||
Seal Strength | 410 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
410 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
ExxonMobil Oppalyte™ 40MD447 OPP Film Product Description: A coextruded super white opaque, modified higher density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for u.. |