ExxonMobil Metallyte™ 38MW480 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Metallyte™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Metallyte™ 38MW480 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque biaxially oriented polypropylene film, metalized on one side.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Outstanding opacity and light barrierConsistent and low COFExcellent metal appearanceBright white background one sideVery good moisture barrierExcellent adhesion of aluminum to filmExtra high yieldGood seal integrity and high seal strengthExcellent support for cold seal with high seal strengthFeatures:In Lamination Lap SealableLight BarrierMoisture BarrierApplications:BakeryBiscuits/Cookie/Crackers Confectionery, Chocolate Confectionery, Gum Confectionery, Sugar Crisps and SnacksFrozen FoodHealth and Beauty CareHousehold and DetergentsIce CreamPet Food Uses: Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 0.497 g/m²/day

@Temperature 38.0 °C
0.0320 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Oxygen Transmission Rate 80.1 cc/m²/day

@Temperature 23.0 °C
5.16 cc/100 in²/day

@Temperature 73.4 °F
Wet, 75% RH; ExxonMobil Method
80.7 cc/m²/day

@Temperature 23.0 °C
5.20 cc/100 in²/day

@Temperature 73.4 °F
0% RH; ExxonMobil Method
Thickness 38.1 microns
1.50 mil
ExxonMobil Method
Coating Weight 23.2 g/m²
14.5 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 140 %
140 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 50 %
50 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.30 GPa
189 ksi
MD; ExxonMobil Method
2.10 GPa
305 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.40
0.40
Unmetallized Side; ExxonMobil Method
Seal Strength 410 g/25 mm

@Pressure 0.276 MPa,
Temperature 130 °C
410 g/in

@Pressure 40.0 psi,
Temperature 266 °F
Otto Brugger, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD 100 MPa
14500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 155 MPa
22500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 6.0 %

@Temperature 135 °C,
Time 432 sec
6.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 6.0 %

@Temperature 135 °C,
Time 432 sec
6.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Optical Density 2.3
2.3
ExxonMobil Method
Gloss 75 %
75 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Heat Seal Range 54°F
36.3 psi, 0.2 sec
Whiteness Index 90
Yield 29800 in2/lb