Polymer Property : Tensile Strength, Ultimate = 104000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 714 MPa

@Thickness 25.4 mm,
Temperature 316 °C
 104000 psi

@Thickness 1.00 in,
Temperature 601 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 715 MPa

@Thickness 12.7 mm,
Temperature 204 °C
 104000 psi

@Thickness 0.500 in,
Temperature 399 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 720 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 649 °C
 104000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1200 °F
Haynes Hastelloy® S alloy, flat products
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate 718 MPa

@Temperature 400 °C
 104000 psi

@Temperature 752 °F
Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed
Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate 717 MPa

@Thickness 6.30 mm,
Temperature 204 °C
 104000 psi

@Thickness 0.248 in,
Temperature 399 °F
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang..
Tensile Strength, Ultimate 716 MPa

@Thickness 12.7 mm,
Temperature 260 °C
 104000 psi

@Thickness 0.500 in,
Temperature 500 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 720 MPa

@Temperature 550 °C
 104000 psi

@Temperature 1020 °F
 Precipitation Hardened prior to test
Special Metals NIMONIC® Alloy PE16
A precipitation-hardenable nickel-iron-chromium alloy with an addition of molybdenum for solid-solution strengthening. It has good strength and oxidation resistance at temperatures to about 1380°..
Tensile Strength, Ultimate 719 MPa

@Thickness 12.7 mm,
Temperature 204 °C
 104000 psi

@Thickness 0.500 in,
Temperature 399 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Tensile Strength, Ultimate 717 MPa

@Temperature 249 °C
 104000 psi

@Temperature 480 °F
 Cold Worked
ATI Wah Chang TI-3Al-2.5V
Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an..