Polymer Property : Tensile Strength, Ultimate = 116000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	798 MPa @Thickness 25.4 mm, Temperature 93.0 Â°C	116000 psi @Thickness 1.00 in, Temperature 199 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Bar, Hot Rolled and Solution Annealed HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	800 MPa @Thickness 19.0 mm, Temperature 260 Â°C	116000 psi @Thickness 0.750 in, Temperature 500 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	800 MPa @Thickness 6.35 mm, Temperature 20.0 Â°C	116000 psi @Thickness 0.250 in, Temperature 68.0 Â°F
Haynes HastelloyÂ® C-22Â® alloy, transverse, GTAW weldment, sheet - plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	799 MPa @Thickness 3.20 mm, Temperature 25.0 Â°C	116000 psi @Thickness 0.126 in, Temperature 77.0 Â°F	as welded
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	800 - 950 MPa @Diameter 101 - 210 mm	116000 - 138000 psi @Diameter 3.98 - 8.27 in	Rm., un-machined
Assab Steels 709M Machinery Steel ASSAB 709M is an alloyed machinery steel with high strength in small and medium sizes. As standard ASSAB 705M is supplied tough hardened requiring no further heat treatment. It can be oil hardened t..
Tensile Strength, Ultimate	801 MPa @Thickness 3.20 mm, Temperature 20.0 °C	116000 psi @Thickness 0.126 in, Temperature 68.0 °F
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..