Polymer Property : Tensile Strength, Ultimate = 122000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	841 MPa @Temperature 288 °C	122000 psi @Temperature 550 °F	Dry; ASTM D3039
Renegade Materials Corporation MVK-14 Polyimide FreeForm™ T650-35 8HS Carbon Fabric MVK-14 polyimide prepregs are a more affordable and easier-to-process, non-carcinogenic alternative to PMR-15 and other older polyimide chemistries. MVK-14 offers a more durable alternative to high-..
Tensile Strength, Ultimate	838 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	122000 psi @Thickness 0.500 in, Temperature 77.0 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	844 MPa @Thickness 1.10 - 1.60 mm, Temperature 20.0 Â°C	122000 psi @Thickness 0.0433 - 0.0630 in, Temperature 68.0 Â°F
Haynes HastelloyÂ® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	841 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	122000 psi @Thickness 0.500 in, Temperature 77.0 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	841 MPa @Thickness 3.20 mm, Temperature 25.0 Â°C	122000 psi @Thickness 0.126 in, Temperature 77.0 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..