Polymer Property : Tensile Strength, Ultimate = 131000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	904 MPa @Thickness 1.45 mm	131000 psi @Thickness 0.0571 in
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 760Â°C (1400Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	902 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	131000 psi @Thickness 0.500 in, Temperature 77.0 Â°F	As Welded; Weld/Base Fracture
Haynes 282Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	900 MPa @Temperature 23.0 Â°C	131000 psi @Temperature 73.4 Â°F
Special Metals NIMONICÂ® Alloy PE16 A precipitation-hardenable nickel-iron-chromium alloy with an addition of molybdenum for solid-solution strengthening. It has good strength and oxidation resistance at temperatures to about 1380Â°..
Tensile Strength, Ultimate	900 - 1050 MPa @Diameter <=100 mm	131000 - 152000 psi @Diameter <=3.94 in	Rm., unmachined
Assab Steels 709M Machinery Steel ASSAB 709M is an alloyed machinery steel with high strength in small and medium sizes. As standard ASSAB 705M is supplied tough hardened requiring no further heat treatment. It can be oil hardened t..
Tensile Strength, Ultimate	902 MPa @Temperature 23.0 °C	131000 psi @Temperature 73.4 °F
ATI Allegheny Ludlum Stainless Steel Type 201, 10% Cold Work (UNS S20100) Allegheny Ludlum Type 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201 provides advantages over the 18-8 grades in certain applications. Lower cost manganese an..
Tensile Strength, Ultimate	902 MPa @Temperature 600 °C	131000 psi @Temperature 1110 °F
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..