ATI Allegheny Ludlum Stainless Steel Type 201, 10% Cold Work (UNS S20100)

Category Metal , Ferrous Metal , Stainless Steel , T S20000 Series Stainless Steel
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum Stainless Steel Type 201, 10% Cold Work (UNS S20100).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Allegheny Ludlum Type 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201 provides advantages over the 18-8 grades in certain applications. Lower cost manganese and nitrogen additions are partial substitutes for nickel making them more economical alloys. Because they possess a very desirable combination of economy plus good mechanical properties and corrosion resistance properties, they have been used in a wide variety of consumer and transportation applications.This austenitic structure achieves significant strengthening through cold working of the material to produce the transformation to a stronger martensitic structure. Type 201 is resistant to a wide variety of mild to moderately corrosive media.Typical applications for Types 201 and 201L are cookware bodies/lids, hose clamps, piston rings, transit car structural member, transit car roofing/siding, thermal window spacers, air bag containers, and truck trailer posts and door frames.Information provided by Allegheny Ludlum Corporation.
Physical Properties Metric English Comments
Density 7.86 g/cc
0.284 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 28.5

@Temperature 23.0 °C
28.5

@Temperature 73.4 °F
28.5

@Temperature 23.0 °C
28.5

@Temperature 73.4 °F
Tensile Strength, Ultimate 856 MPa

@Temperature 23.0 °C
124000 psi

@Temperature 73.4 °F
902 MPa

@Temperature 23.0 °C
131000 psi

@Temperature 73.4 °F
Tensile Strength, Yield 645 MPa

@Temperature 23.0 °C
93500 psi

@Temperature 73.4 °F
678 MPa

@Temperature 23.0 °C
98300 psi

@Temperature 73.4 °F
Elongation at Break 31.3 %

@Temperature 23.0 °C
31.3 %

@Temperature 73.4 °F
32 %

@Temperature 23.0 °C
32 %

@Temperature 73.4 °F
Modulus of Elasticity 210 GPa
30500 ksi
Compressive Yield Strength 441 MPa
64000 psi
Thermal Properties Metric English Comments
CTE, linear 16.6 µm/m-°C

@Temperature 20.0 - 100 °C
9.22 µin/in-°F

@Temperature 68.0 - 212 °F
18.0 µm/m-°C

@Temperature 20.0 - 316 °C
10.0 µin/in-°F

@Temperature 68.0 - 601 °F
18.0 µm/m-°C

@Temperature 20.0 - 358 °C
10.0 µin/in-°F

@Temperature 68.0 - 676 °F
20.3 µm/m-°C

@Temperature 20.0 - 871 °C
11.3 µin/in-°F

@Temperature 68.0 - 1600 °F
Specific Heat Capacity 0.502 J/g-°C

@Temperature 0.000 - 100 °C
0.120 BTU/lb-°F

@Temperature 32.0 - 212 °F
Thermal Conductivity 16.3 W/m-K

@Temperature 100 °C
113 BTU-in/hr-ft²-°F

@Temperature 212 °F
23.0 W/m-K

@Temperature 500 °C
160 BTU-in/hr-ft²-°F

@Temperature 932 °F
Melting Point 1400 - 1455 °C
2550 - 2651 °F
Solidus 1400 °C
2550 °F
Liquidus 1455 °C
2651 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.15 %
<= 0.15 %
Chromium, Cr 16 - 18 %
16 - 18 %
Iron, Fe 72 %
72 %
as balance
Manganese, Mn 5.5 - 7.5 %
5.5 - 7.5 %
Nickel, Ni 3.5 - 5.5 %
3.5 - 5.5 %
Nitrogen, N <= 0.25 %
<= 0.25 %
Silicon, Si <= 1.0 %
<= 1.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000670 ohm-cm
0.0000670 ohm-cm
Magnetic Permeability 1.048
1.048
D.C. Permeability (m at 200 H)