Polymer Property : Tensile Strength, Ultimate = 724 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	724 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	105000 psi @Thickness 0.500 in, Temperature 77.0 Â°F
Haynes HastelloyÂ® G-35Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOYÂ® G-35Â® alloy was designed to resist â€œwet processâ€ phosphoric acid, which is widely used in the production of fertilizers. Tests indicat..
Tensile Strength, Ultimate	724 MPa @Diameter 12.7 mm, Temperature 25.0 Â°C	105000 psi @Diameter 0.500 in, Temperature 77.0 Â°F	As welded
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	724 MPa @Temperature 649 °C	105000 psi @Temperature 1200 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate	724 MPa @Temperature 649 °C	105000 psi @Temperature 1200 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate	724 MPa @Temperature 93.0 °C	105000 psi @Temperature 199 °F
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	724 MPa @Diameter 50.8 mm, Temperature 25.0 °C	105000 psi @Diameter 2.00 in, Temperature 77.0 °F
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..