Polymer Property : Tensile Strength, Ultimate = 105000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 724 MPa

@Thickness 12.7 mm,
Temperature 25.0 °C
 105000 psi

@Thickness 0.500 in,
Temperature 77.0 °F
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate
Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicat..
Tensile Strength, Ultimate 725 MPa

@Thickness 25.4 mm,
Temperature 260 °C
 105000 psi

@Thickness 1.00 in,
Temperature 500 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 727 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 538 °C
 105000 psi

@Thickness 0.374 - 1.00 in,
Temperature 1000 °F
Haynes Hastelloy® S alloy, flat products
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate 726 MPa

@Temperature 540 °C
 105000 psi

@Temperature 1000 °F
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C)
Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas..
Tensile Strength, Ultimate 721 MPa

@Temperature 200 °C
 105000 psi

@Temperature 392 °F
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed
Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate 724 MPa

@Diameter 12.7 mm,
Temperature 25.0 °C
 105000 psi

@Diameter 0.500 in,
Temperature 77.0 °F
 As welded
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate 725 MPa

@Thickness 12.7 mm,
Temperature 204 °C
 105000 psi

@Thickness 0.500 in,
Temperature 399 °F
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang..
Tensile Strength, Ultimate 727 MPa

@Thickness 9.50 mm,
Temperature 204 °C
 105000 psi

@Thickness 0.374 in,
Temperature 399 °F
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang..
Tensile Strength, Ultimate 723 MPa

@Thickness 12.7 mm,
Temperature 204 °C
 105000 psi

@Thickness 0.500 in,
Temperature 399 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 723 MPa

@Diameter 12.7 mm,
Temperature 93.0 °C
 105000 psi

@Diameter 0.500 in,
Temperature 199 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 724 MPa

@Temperature 649 °C
 105000 psi

@Temperature 1200 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy
Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate 724 MPa

@Temperature 649 °C
 105000 psi

@Temperature 1200 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy
Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate 723 MPa

@Thickness 19.1 mm,
Temperature 204 °C
 105000 psi

@Thickness 0.752 in,
Temperature 399 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Tensile Strength, Ultimate 724 MPa

@Temperature 93.0 °C
 105000 psi

@Temperature 199 °F
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C)
Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate 724 MPa

@Diameter 50.8 mm,
Temperature 25.0 °C
 105000 psi

@Diameter 2.00 in,
Temperature 77.0 °F
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C)
Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..