Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 727 MPa @Thickness 9.50 - 25.4 mm, Temperature 538 °C |
105000 psi @Thickness 0.374 - 1.00 in, Temperature 1000 °F |
|
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Ultimate | 727 MPa @Thickness 9.50 mm, Temperature 204 °C |
105000 psi @Thickness 0.374 in, Temperature 399 °F |
|
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |