Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 550 MPa @Diameter 105 - 200 mm |
79800 psi @Diameter 4.13 - 7.87 in |
|
United Cast Bar Unibar 600-3 Continuously Cast Spheroidal Graphite Iron Offers reasonable machinability and excellent surface finish combined with higher wear resistance, strength & heat treatment. Noise and vibration damping are good in this grade.Unibar 600-3 can be .. |
|||
Tensile Strength | 550 MPa @Diameter 205 - 600 mm |
79800 psi @Diameter 8.07 - 23.6 in |
|
United Cast Bar Unibar 600-3 Continuously Cast Spheroidal Graphite Iron Offers reasonable machinability and excellent surface finish combined with higher wear resistance, strength & heat treatment. Noise and vibration damping are good in this grade.Unibar 600-3 can be .. |
|||
Tensile Strength | >= 550 MPa @Thickness 76.2 - 127 mm |
>= 79800 psi @Thickness 3.00 - 5.00 in |
Tempers T651 / T652 |
Constellium Alumold® 500 Rolled Aluminum The Alumold® 500 alloy has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important prop.. |
|||
Tensile Strength | 550 MPa @Thickness 25.0 - 100 mm |
79800 psi @Thickness 0.984 - 3.94 in |
Typical Strength |
Constellium Certal® Thick Aluminum Plate Certal® thick plates have been optimized to provide excellent machinability, shape stability and high strength. Certal® is therefore ideal for industrial tools. Applications include injection and .. |
|||
Tensile Strength | >= 550 MPa @Thickness 25.0 - 40.0 mm |
>= 79800 psi @Thickness 0.984 - 1.57 in |
|
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |