Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
NCMT NanoPAC™ G3000 High Performance Polypropylene Nanocomposite Applications: Automobile Construction MaterialInformation provided by Nano Composite Materials Technology Limited |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
Global AS-320-PC Acrylonitrile Styrene, High Chemical/High Heat Resistance Grade Description-transparent, medium impact resistance, high hardness, good stiffness, high heat resistance, good chemical resistanceApplications-sanitary products, electrical partsInformation provided b.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH0 Flame retardant copolyamide 66/6, unreinforced, heat stabilized, for injection molding.This phosphorus and halogen free flame retardant grade, UL 94 VO (0.4 mm), offers excellent filling qualities a.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | 5mm/min; ISO 527 |
Styrolution Terblend® N NG-04 20% Glass Filled ABS/PA6 (Dry) Terblend N NG-04 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, low mold shrinkage and high heat resistance.Information provided by STYROLUTION, which is a joint ven.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
Sumitomo Bakelite North America RX® 611 Fiberglass Reinforced Phenolic RX 611 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type MFH.Information supplied by Sumitomo.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
Wellman Wellamid® 22L-N Unfilled Nylon 66, Lubricated Typical Applications: Automotive components, gears, switches, bearings, pulleys, fasteners, electrical coil forms, chain-saw hand guards, cable ties, furniture hardware, small appliance housings, ae.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 |
DSM Akulon® K222-KGV4 /A PA6-GF20 FR(30) 20% Glass Reinforced, Heat Stabilized, Flame Retardant (Halogen-phosphorous-free) |
|||
Tensile Strength, Ultimate | 80.0 - 94.0 MPa | 11600 - 13600 psi | |
Dow CYCLOTENE™ 3022-57 Bisbenzocyclobutene (BCB) Electronic Resin This product was developed for use as spin-on dieletric materials in microelectronic fabrication.Information provided by Dow |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-8S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-30EH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-30UH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-35 Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-35H Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-35SH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-40H Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-40SH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-42 Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-50 Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-6S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-38H Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-38M Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-40 Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 - 150 MPa @Temperature 70.0 - 175 °C |
11600 - 21800 psi @Temperature 158 - 347 °F |
Average value: 104 MPa Grade Count:3 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 80.0 - 150 MPa @Time 180000 - 7.20e+7 sec |
11600 - 21800 psi @Time 50.0 - 20000 hour |
Average value: 104 MPa Grade Count:3 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-33M Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-48 Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 - 123 MPa @Temperature 150 - 250 °C |
11600 - 17800 psi @Temperature 302 - 482 °F |
Average value: 97.0 MPa Grade Count:2 |
Overview of materials for Epoxy Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Molding Compound". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
Sumitomo Bakelite North America FM 4004F Fiberglass and Mineral Reinforced Phenolic Novolac FM 4004F is a fiberglass and mineral reinforced phenolic novolac compound with improved strength properties over FM 4004. This compound exhibits excellent dimensional stability and good strength at.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 627 Nylon 6/6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |