Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 54.5 - 150 MPa | 7900 - 21800 psi | Average value: 97.2 MPa Grade Count:42 |
Overview of materials for Polyetheretherketone, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Unreinforced". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Ultimate | 62.1 - 150 MPa | 9000 - 21800 psi | Average value: 102 MPa Grade Count:7 |
Overview of materials for Polyamide-Imide, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Tensile Strength, Ultimate | 27.6 - 150 MPa | 4000 - 21800 psi | Average value: 84.3 MPa Grade Count:10 |
Overview of materials for Polyphenylene Sulfide (PPS); Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS); Molded". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Ultimate | 140 - 150 MPa @Temperature 80.0 - 80.0 °C |
20300 - 21800 psi @Temperature 176 - 176 °F |
Average value: 128 MPa Grade Count:4 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Tensile Strength, Ultimate | 38.0 - 150 MPa | 5510 - 21800 psi | Average value: 78.2 MPa Grade Count:87 |
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Ultimate | 60.0 - 150 MPa @Temperature 120 - 200 °C |
8700 - 21800 psi @Temperature 248 - 392 °F |
Average value: 103 MPa Grade Count:7 |
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 45.0 - 150 MPa | 6530 - 21800 psi | Average value: 70.5 MPa Grade Count:22 |
Overview of materials for Nylon 6, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, PTFE Filled". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Tensile Strength, Ultimate | 80.0 - 150 MPa @Temperature 70.0 - 175 °C |
11600 - 21800 psi @Temperature 158 - 347 °F |
Average value: 104 MPa Grade Count:3 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 80.0 - 150 MPa @Time 180000 - 7.20e+7 sec |
11600 - 21800 psi @Time 50.0 - 20000 hour |
Average value: 104 MPa Grade Count:3 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 81.4 - 150 MPa | 11800 - 21800 psi | Average value: 118 MPa Grade Count:23 |
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 50.0 - 150 MPa | 7250 - 21800 psi | Average value: 125 MPa Grade Count:18 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Tensile Strength, Ultimate | 75.0 - 150 MPa | 10900 - 21800 psi | Average value: 102 MPa Grade Count:29 |
Overview of materials for Polyethylene Terephthalate (PET), 20% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 20% Glass Reinforced". Specific grades with glass content between 15% .. |
|||
Tensile Strength, Ultimate | 60.0 - 150 MPa @Temperature 60.0 - 230 °C |
8700 - 21800 psi @Temperature 140 - 446 °F |
Average value: 100 MPa Grade Count:8 |
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are.. |
|||
Tensile Strength, Ultimate | 30.0 - 150 MPa | 4350 - 21800 psi | Average value: 96.4 MPa Grade Count:97 |
Overview of materials for Polypropylene with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Glass Fiber Filler". Specific grades with glass content between 35% and 44% are i.. |
|||
Tensile Strength, Ultimate | 20.0 - 150 MPa | 2900 - 21800 psi | Average value: 50.1 MPa Grade Count:83 |
Overview of materials for Polypropylene, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum .. |