Polymer Property : Tensile Strength, Ultimate = 12.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	12.8 MPa	1860 psi	ASTM D412
Multibase Multi-Flex® TPE A 9009 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	12.8 MPa	1860 psi	ASTM D638-95
Multibase Multi-Flex® TPO 1047-1000 COMPOUND The burn rate is 0.53 in/min; ASTM FM VSS 302.Data provided by Multibase.
Tensile Strength, Ultimate	12.8 MPa	1860 psi	ASTM D638-95
Multibase Multi-Flex® TPO 1047-2000 GRAPHITE The burn rate is 0.55 in/min; ASTM FM VSS 302.Data provided by Multibase.
Tensile Strength, Ultimate	12.8 MPa	1860 psi	20" / min.; ASTM D-683-95
Multibase Multi-Flex® TPO D 4502 C Black Multi-Flex® D 4502 Black is based on Shell's Kraton G polymer and is suitable for applications for the automotive industry. It exhibits excellent paintability adhesion.Data provided by Multibase.
Tensile Strength, Ultimate	12.8 MPa	1860 psi	ASTM D638
Multibase Multi-Pro® 4810 C White 47.7% Filler Content Polypropylene Moisture content is 0.04%. Data provided by Multibase.
Tensile Strength, Ultimate	12.8 MPa	1850 psi
Sylvin Technologies 9950-90 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	12.8 MPa	1850 psi	ASTM D638
Dow AMPLIFY™ EA 102 Ethylene-ethyl Acrylate (EEA) AMPLIFY™ EA 102 Functional Polymer is produced via a high pressure reactor. It exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. This polymer..