Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 12.8 MPa | 1860 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 9009 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 12.8 MPa | 1860 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO 1047-1000 COMPOUND The burn rate is 0.53 in/min; ASTM FM VSS 302.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 12.8 MPa | 1860 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO 1047-2000 GRAPHITE The burn rate is 0.55 in/min; ASTM FM VSS 302.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 12.8 MPa | 1860 psi | 20" / min.; ASTM D-683-95 |
Multibase Multi-Flex® TPO D 4502 C Black Multi-Flex® D 4502 Black is based on Shell's Kraton G polymer and is suitable for applications for the automotive industry. It exhibits excellent paintability adhesion.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 12.8 MPa | 1860 psi | ASTM D638 |
Multibase Multi-Pro® 4810 C White 47.7% Filler Content Polypropylene Moisture content is 0.04%. Data provided by Multibase. |