Polymer Property : Tensile Strength, Ultimate = 177 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	177 - 200 MPa	25600 - 29000 psi	Average value: 187 MPa Grade Count:5
Overview of materials for Polyetherimide (PEI), 40% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 40% Glass Fiber". Specific grades with glass content between 35% and 44% are included. E..
Tensile Strength, Ultimate	177 MPa	25700 psi	DIN 53455; ASTM D638
Kolon KopaÂ® KN133HB55 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c..
Tensile Strength, Ultimate	177 MPa	25700 psi	ASTM D638
Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, at 50% RH (di AMODEL AF-1145 V0 is a 45% glass reinforced, flame retarded polyphthalamide (PPA) which exhibits a high heat distortion temperature, high tensile strength and flexural modulus. The material is rela..
Tensile Strength, Ultimate	177 MPa	25700 psi	5mm/min; ISO 527
BASF Ultramid® B3WG6 BK00564 BGVW 30% Glass Filled PA6 (Dry) Ultramid B3WG6 BK00564 BGVW is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade.