Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 122 MPa | 17700 psi | ASTM Data |
Dow Questra® EA514 High Heat Syndiotactic Polystyrene, 40% Glass Filled
(discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve.. |
|||
Tensile Strength, Ultimate | 122 MPa | 17700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1010GN2-15 NAT PA6-GF15 FR(17) 15% Glass Reinforced, Flame Retardant, Injection Molding, High Flow |
|||
Tensile Strength, Ultimate | 122 MPa | 17700 psi | 5mm/min; ISO 527 |
BASF Ultramid® A3EG3 BK00564 15% Glass Filled PA66 (Dry) Ultramid A3EG3 BK00564 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Tensile Strength, Ultimate | 122 MPa | 17700 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3GM35 BKQ649 23220 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 BKQ649 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. |