Polymer Property : Tensile Strength, Ultimate = 18.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	18.3 MPa	2650 psi	ASTM D638-95
Multibase Multi-Pro® 5002 X White 50% Filler Content Polypropylene Multi-Pro 5002 X White is an extrusion grade filled polypropylene that has good stiffness as well as excellent impact properties. It can be made in any color.Data provided by Multibase.
Tensile Strength, Ultimate	18.3 MPa	2650 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman M3007-P Polyethylene (discontinued **) M3007-P is suggested for applications such as spiral-wound can linings, release paper, and photographic paper. M3007-P Has been found to exhibit good barrier properties, temperature resistance, and..
Tensile Strength, Ultimate	18.3 MPa	2650 psi	ASTM D412
Multibase Multi-FlexÂ® RP 6568 B2 Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
Tensile Strength, Ultimate	18.3 MPa	2650 psi
Sylvin Technologies 8950-95 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	18.3 MPa	2650 psi
Sylvin Technologies 9600-90 Clear PVC Molding Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	18.3 MPa @Time 605000 sec	2660 psi @Time 168 hour	Heat Aging; ASTM D 412/ASTM D 573
Zylog Neoplast® 187 FT EB Thermoplastic Vulcanizate Neoplast 187 FT EB is a hard, dynamically vulcanized thermoplastic vulcanizate (TPV), based on polyolefin chemistry, and is intended for Injection Molding, Blow Molding and Extrusion applications.Ro..
Tensile Strength, Ultimate	18.3 MPa	2650 psi	Molded property
Dow DOWLEX™ 2037 Linear Low Density Polyethylene, Cast Film Grade DOWLEX® 2037 Polyethylene is a cast film extrusion resin for high stiffness film applications. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2a when used unmodified and according to good..
Tensile Strength, Ultimate	18.3 MPa	2650 psi	ASTM D412
Colorite Polymers CS904015 Wire and Cable Jacket Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai..
Tensile Strength, Ultimate	18.3 MPa	2650 psi	Cured 7 min at 177°C and Post Cured 2 hr at 232°C
DuPont Performance Polymers VTR 8550 (GFLT-S) Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinued FormulationVTR-8550