Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 607 MPa @Temperature 204 °C |
88000 psi @Temperature 399 °F |
|
Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 607 MPa | 88000 psi | |
Universal Wire Works 310 Mo Stainless Steel Electrode Universal 310 Mo electrodes are used for the welding of the clad side of types 316, 316L, and 317 clad steels. This alloy is also used for welding other molybdenum bearing stainless steels to mild o.. |
|||
Tensile Strength, Ultimate | 607 MPa | 88000 psi | |
Universal Wire Works 316 Stainless Steel (AMS 5692) Filler Metal Universal 316 is a chromium-nickel alloy with large amounts of molybdenum added for superior corrosion resistance and strength. The corrosion resistance is superior to types 302 and 304 making 316 t.. |
|||
Tensile Strength, Ultimate | 607 MPa | 88000 psi | |
Universal Wire Works 316 Stainless Steel Electrode Universal 316 electrodes are widely used in the fabrication of type 316 stainless steel as used in the manufacture of parts and equipment for the chemical and process industries. The weld metal matc.. |
|||
Tensile Strength, Ultimate | 607 MPa | 88000 psi | |
Universal Wire Works 317L Stainless Steel Electrode Universal 317L electrodes are slightly higher in alloy content than type 316L, particularly in molybdenum and are used primarily for welding type 317 stainless steel. This electrode is used extensiv.. |
|||
Tensile Strength, Ultimate | 607 - 710 MPa | 88000 - 103000 psi | |
Eagle Brass 510 Phosphor Bronzes 5% A, Extra Hard Alloy C510 is an alloy with good strength, formability and stress relaxation characteristics, and solderability. Applications include electronic parts, springs, switches, contacts and fasteners.Info.. |
|||
Tensile Strength, Ultimate | >= 607 MPa | >= 88000 psi | |
Eagle Brass 735 Nickel Silver 18%, Extra Spring 735 is used for coinage, name plates, zippers, flatware, and fashion jewelry.Information provided by Eagle Brass Company |
|||
Tensile Strength, Ultimate | 607 - 696 MPa | 88000 - 101000 psi | |
Eagle Brass 770 Nickel Silver 18%, 3/4 Hard 770 has good cold forming properties, is tarnish resistant and has very good spring properties. 770 does not become subject to embrittlement at lower temperature and it has excellent corrosion resi.. |
|||
Tensile Strength, Ultimate | 607 MPa | 88000 psi | Calculated from tenacity |
DuPont™ Nomex® 430 1200 Denier Aramid Yarn A high crystallinity natural filament yarn of NOMEX with higher strength and chemical resistance than staple spun yarns. Type 430 is used where the aesthetics and properties of a filament yarn are .. |
|||
Tensile Strength, Ultimate | 607 MPa | 88000 psi | |
Carpenter 20-Mo6® Stainless Steel, Strip Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, .. |
|||
Tensile Strength, Ultimate | 607 MPa @Temperature 149 °C |
88000 psi @Temperature 300 °F |
|
ATI Allegheny Ludlum AL 2003™ Duplex Stainless Steel Characteristics: superior stress corrosion cracking resistance to Types 316 and 317, yield strength double that of conventional austenitic stainless steel, good corrosion resistance, good chloride s.. |
|||
Tensile Strength, Ultimate | 607 MPa @Temperature 538 °C |
88000 psi @Temperature 1000 °F |
|
Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |