Polymer Property : Tensile Strength, Ultimate = 785 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	785 MPa @Temperature 316 Â°C	114000 psi @Temperature 600 Â°F
Kennametal Stellite StelliteÂ® 6K 12.7 or 22.2 mm plate 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g..
Tensile Strength, Ultimate	785 MPa @Temperature 540 Â°C	114000 psi @Temperature 1000 Â°F
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	785 MPa	114000 psi
Haynes 25 alloy, room temperature sheet after 100 hours of 870Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	>= 785 MPa	>= 114000 psi
Crucible Steel 21-12N (JIS SUH37) Martensitic Steel Information provided by Crucible Specialty Metals.
Tensile Strength, Ultimate	785 MPa @Temperature 23.0 °C	114000 psi @Temperature 73.4 °F
ATI Allegheny Ludlum Stainless Steel Type 201L, Annealed (UNS S20103) Allegheny Ludlum Types 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201L provides advantages over the 18-8 grades in certain applications. Lower cost manganese ..
Tensile Strength, Ultimate	785 MPa	114000 psi	50% Cold Worked
AK Steel 439 ULTRA FORM® Stainless Steel AK Steel 439 ULTRA FORM™ was developed for applications requiring oxidation and corrosion resistance superior to Type 409 as well as superior formability to AK Steel 439 Stainless Steel. As a resul..
Tensile Strength, Ultimate	785 MPa	114000 psi
Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..