Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 951 - 1090 MPa | 138000 - 158000 psi | |
Materion Alloy 390 Beryllium Nickel Strip Alloy 390 was specifically designed for high power applications, providing a unique combination of high strength and high conductivity. Increasing power requirements are driving the need for lower c.. |
|||
Tensile Strength, Ultimate | 951 MPa | 138000 psi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Tensile Strength, Ultimate | 951 MPa @Temperature 199 °C |
138000 psi @Temperature 390 °F |
(hardened to 310 HB) |
Bohler-Uddeholm HOLDER Pre-hardened Holder Tool Steel Chromium-molybdenum alloyed steelA pre-hardened steel with very good machinability supplied at ~300 HB for clamping and holding plates and blocks.Holder is characterized by: Excellent machinability.. |
|||
Tensile Strength, Ultimate | 951 - 1100 MPa | 138000 - 160000 psi | hardened to 300 HB |
Bohler-Uddeholm P20 PREMIUM MODIFIED Pre-hardened Mold Steel Cr-Mo alloyed steelP20 Modified offers the following benefits:No hardening risksNo hardening costsTime saving, e.g. no waiting for heat treatmentLower tool cost (e.g. no distortion to rectify)Modifi.. |
|||
Tensile Strength, Ultimate | 951 MPa | 138000 psi | Long. |
ATI Wah Chang 425™ Titanium Alloy, Tubular Extruded, Mill Annealed ATI 425™ titanium is an innovative high strength alloy that has strength comparable to Ti-6-4, yet has the advantage that it can be cold worked. Originally developed for armor plate for ballistic p.. |
|||
Tensile Strength, Ultimate | 951 MPa @Temperature 400 °C |
138000 psi @Temperature 752 °F |
|
Kennametal Stellite Nucalloy® 430 High-Silicon Nickel-Base Hardfacing Alloy Applications include components of chemical processing.Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness .. |