Mechanical Properties	Metric	English	Comments
Shear Strength	13.4 MPa	1950 psi	Bond, Al to Al, RT Cure
Master Bond EP34AO Epoxy Compound Withstands High Temperatures Description: Master Bond Polymer System EP34AO is a room temperature curing, two component epoxy compound for high temperature bonding and sealing applications especially where thermal conductivity ..
Shear Strength	13.4 MPa	1950 psi	Long Beam Shear, L Direction
Hexcel® HexWeb® HDC-660 - 3/16 - 17.5 (R2) Heavy Density Core Designation: Material-Cell Size (inches)-DensityHexWeb® HDC is a fabric reinforced honeycomb, typically made from either fiberglass or carbon prepreg. A thermosetting node adhesive is used with eit..
Shear Strength	13.4 MPa	1950 psi	CRS Overlap, Tap Water at RT
3M Scotch-Weld™ 183 B/A Green Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1838 B/A is a controlled flow product. This epoxy adhesives are two-part, room temperature curing structural adhesives with high shear strengths and excellent envir..
Shear Strength	13.4 MPa	1950 psi	Overlap, Aluminum (1/16" thick), Adhesive Failure
3M Scotch-Weld™ DP8010NS Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010NS is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polyprop..
Shear Strength	13.4 MPa	1950 psi	Tensile lap
Abatron AboCast 8503-9/AboCure 8503-9 5-Minute Epoxy AboCast 8503-9/AboCure 8503-9 is a very-fast-hardening 2-component epoxy adhesive, casting, and patching compound. It is a neutral-buff colored, non-sag, mineral-filled putty to be applied with trow..
Shear Strength	13.4 MPa	1950 psi	Overlap, CRS/CRS after 7 days of Immersion in Machine Oil
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability ..
Shear Strength	13.4 MPa @Temperature 81.0 - 83.0 °C	1950 psi @Temperature 178 - 181 °F	Etched Aluminum Overlap, 0.8% (Rust Inhibitor)/ 99.2% Tap Water Immersion for 30 days
3M Scotch-Weld™ EC-1386 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive EC-1386 is a one-part, 100% solids, thermosetting liquid adhesive.Information provided by 3M
Shear Strength	13.4 MPa	1950 psi	Overlap, Aluminum, Adhesive Failure
3M Scotch-Weld™ Medium Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t..
Shear Strength	13.4 MPa @Temperature 32.0 °C	1950 psi @Temperature 89.6 °F	Overlap, Oak, 90% RH, Substrate/Adhesive Failure
3M Scotch-Weld™ Medium Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t..
Shear Strength	13.4 MPa	1950 psi	Overlap, Etched Al, Tap water at RT for 30 days
3M Scotch-Weld™ 2216 B/A Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel..