Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.860 GPa | 125 ksi | 1% Strain Value from rotomolded samples; ASTM D790 |
NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, .. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | 1% Strain Value from rotomolded samples; ASTM D790 |
NOVA Chemicals Novapol® TR-0338-UIG Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, .. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-LOY M3000C PP LNP* STAT-LOY* M3000C is a compound based on unfilled Polypropylene resin. Added features of this grade include: Clean Compound System, Antistat. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | Tangent - 16:1 span:depth, 0.5 in/min; ASTM D-790 |
Chevron Phillips Marlex® HMN TR-942/942G Polyethylene; HDPE High density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and fair flowLong-term UV stabilizationExcellent impact stren.. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | ASTM D790 |
Covestro Bayflex® 110-50 Polyurethane Elastomeric RIM, 15% Mineral Filled, MDI-based 2-Component Liquid System Mineral filler is RRIMGLOS® 10013. 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialSc.. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | ASTM D790A |
BP Amoco Acctuf® 3541 Impact Copolymer Polypropylene
(discontinued **) Suggested fabrication methods: Injection moldingFeatures: General purpose, High melt flowComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection molded sam.. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | 0.05 in/min, 1x3"; ASTM D790 |
LyondellBasell DEXFLEX® 711 TPO Description: DEXFLEX® 711 is a thermoplastic olefinic elastomer compounded with post-industrial/post-consumer recycled materials. It is designed for use in applications that are (non-color matched.. |
|||
Flexural Modulus | 0.860 GPa | 125 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |