Polymer Property : Flexural Modulus = 1040 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	7.18 GPa	1040 ksi	ASTM D790
PolyOne Stat-Tech™ CTX-1125 Natural Acrylonitrile Butadiene Styrene (ABS) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Flexural Modulus	7.20 GPa	1040 ksi	ISO 178
Nilit RECONYL A GV30 Recycled nylon 6.6 for injection molding, 30% glass fiber reinforced Recycled nylon 6.6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Modulus	7.20 - 27.6 GPa	1040 - 4000 ksi	Average value: 14.0 GPa Grade Count:45
Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled". Specific grades with glass content between 35% an..
Flexural Modulus	7.20 - 19.0 GPa @Temperature -40.0 - 80.0 °C	1040 - 2760 ksi @Temperature -40.0 - 176 °F	Average value: 13.4 GPa Grade Count:1
Overview of materials for Nylon 66, 30% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Carbon Fiber Filled". Specific grades with carbon fiber content between 25% and 34% are in..
Flexural Modulus	7.20 GPa	1040 ksi
Lehmann & Voss NylatronÂ® MR 2007 Polyamide 6, with mineral filler Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Low warpage.Isotropic shrinkage characteristics.Information provided by Lehmann & Voss & Co.KG
Flexural Modulus	7.20 GPa	1040 ksi	ISO 178
Solvay TECHNYLÂ® C 216 V40 PA6, 40% glass fiber, Conditioned Description: TECHNYLÂ® C 216 V40 is a polyamide 6, reinforced with 40% of glass fiber, for injection molding. This product is available in black color.Benefits: The product offers a good combinati..
Flexural Modulus	7.20 GPa	1040 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RX05050 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RX05050 is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Modulus	7.20 GPa	1040 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East) 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu..
Flexural Modulus	7.20 GPa	1040 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 LNP LUBRILOY* RF206 is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material includes: Wear Resistant.
Flexural Modulus	7.17 GPa @Temperature 100 Â°C	1040 ksi @Temperature 212 Â°F	ISO 178
Solvay Specialty Polymers AmodelÂ® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samp..
Flexural Modulus	7.20 GPa	1040 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® K4560 PBT 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
Flexural Modulus	7.20 GPa	1040 ksi
SPS Guang Zhou PONYLâ„¢ 4001G30 GF30%-PA66 Characteristic: High mechanical properties, superior heat resistance, good dimensional stabilityApplications: Power tool, chassis and E/E partsInformation Provided by SPS (Guang Zhou) Ltd.
Flexural Modulus	7.20 GPa	1040 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF006ER PC (Europe-Africa-Middle East) LNP* Thermocomp* DF006ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Flexural Modulus	7.20 GPa	1040 ksi	2mm/min; ISO 178
Teijin PanliteÂ® BN-8110R Improved Mold Release, Carbon Fiber Reinforced, Flame Resistant Polycarbonate Resin CF 10% reinforced grade, meeting UL 94 V-2. It has excellent strength, stiffness, heat resistance and electric conductivity. Other features are flame retardance, low molding shrinkage and dimensiona..
Flexural Modulus	7.20 GPa	1040 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON MV005SX0 PP (Europe-Africa-Middle East) LNP* VERTON* MV005SX0 is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized.
Flexural Modulus	7.20 GPa	1040 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en..
Flexural Modulus	7.20 GPa	1040 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp EF006R PEI (Europe-Africa-Middle East) LNP* Thermocomp* EF006R is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Mold Release.This data was supplied by SABIC-IP for the Europe-A..
Flexural Modulus	7.17 GPa	1040 ksi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL EM7430 PPE+PS 30% glass reinforced, high flow PPO. Automotive. Energy management material.
Flexural Modulus	7.20 GPa	1040 ksi	ISO 178
Polyram PlusTek RA301G5 Nylon 6.6 for Injection Molding, 25% Glass Fiber Reinforced, Heat Stabilized Heat stabilized, 25% glass fibers reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
Flexural Modulus	7.20 GPa	1040 ksi	DIN 52457
CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Flexural Modulus	7.20 GPa	1040 ksi	DIN 52457
CP-Polymer-Technik Wellamid® 6000/51 GV 30 HWCP 30% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Flexural Modulus	7.20 GPa	1040 ksi	ASTM D790
Ashley Polymers Ashlene® 126 PBT Polyester, 30% Glass Reinforced General purpose 30% glass reinforcement, natural. Colors will modify properties.Data provided by the manufacturer
Flexural Modulus	7.20 GPa	1040 ksi	ASTM D790
Ashley Polymers Ashlene® 630-33GU Nylon 6, 33% Glass Reinforced Nylon 6, 33% glass reinforced resin, utility grade. Also available: 630S - 33GU Heat Stabilized, 630 - 33GBU Black, 630S - 33GBU Black with H.S.Data provided by the manufacturer
Flexural Modulus	7.20 GPa	1040 ksi	ASTM D790
Chem Polymer Chemlon 125-15 MG Nylon 66, 25% Mineral/15% Glass Fiber Reinforced A 25% mineral reinforced, 15% glass fiber reinforced nylon 66 offering excellent rigidity, dimensional stability and tensile strength with improved warpage control in large area parts.Data provided ..
Flexural Modulus	7.20 GPa	1040 ksi	ASTM D790
Ashley Polymers Ashlene® 520-33GU Nylon 66, 33% Glass Reinforced Nylon 66, 33% glass reinforced resin, utility grade for non-critical applications. Also available: 520S - 33GU Heat Stabilized, 520 - 33GBU Black, 520S - 33GBU Black with H.S.Data provided by the m..
Flexural Modulus	7.20 GPa	1040 ksi	ASTM D790
Ashley Polymers Ashlene® P266 PPO, 30% Glass Reinforced A general purpose, 30% glass reinforced PPO resin for injection molding applications.Data provided by the manufacturer
Flexural Modulus	7.20 GPa	1040 ksi	ASTM D790
Chem Polymer Formax 630 G Acetal, 30% Glass Fiber Reinforced A copolymer acetal reinforced with 30% glass fiber for use in applications requiring great strength and rigidity.Data provided by the manufacturer, Chem Polymer.
Flexural Modulus	7.17 GPa @Temperature 100 °C	1040 ksi @Temperature 212 °F	ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer Amodel AS-4133 HN polyphthalamide (PPA) is a non-lubricated, heat stabilized grade that offers fast cycle times and is hot-water moldable. Typical applications include electrical and electronic comp..