Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.65 GPa | 529 ksi | |
Plastcom SLOVAMID 66 C 15 MI PA66, 15% mineral filling Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | |
Plastcom SLOVAMID 66 T 15 MI PA66, 15% mineral filling FeaturesPA 66 with the content of 15 % chemically modified mineral filling and impact modified. Used for holders of electric hand tools, for hobby tools, gears, covers of electric tools, flat produc.. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | ASTM D790 |
Polymer Resources PPX-G10HF Modified-PPO, 10% Glass Reinforced, High Flow Modified-Polyphenylene Oxide, 10% Glass Reinforced, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf.. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® CM8622 PC+ABS (Europe-Africa-Middle East) CYCOLOY* CM8622 is a high heat PC/ABS blend offering high modulus, low CTE and good |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | ISO 178 |
Solvay TECHNYL® B 50 H1 PA66/6, DRY Description: TECHNYL® B 50H1 is an unreinforced melamine cyanurate flame retarded copolyamide 66/6. This product has been heat stabilized and is suitable for injection molding. This product is av.. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ZFL31XXC PPE+PS LNP* LUBRICOMP* ZFL31XXC is a compound based on PPE+PS resin containing 5% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP NF001 PC+ABS (Asia Pacific) LNP* Thermocomp* NF001 is a compound based on PC+ABS Blend resin containing Glass Fiber. |