Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 9.14 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2310EPR PEI 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Flexural Modulus | 9.14 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2310EPR PEI (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Flexural Modulus | 9.14 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2310EPR PEI (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing. |
|||
Flexural Modulus | 9.14 GPa | 1330 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PF007 PA 6 LNP* THERMOCOMP* PF007 is a compound based on Nylon 6 resin containing 35% Glass Fiber. |
|||
Flexural Modulus | 9.14 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66 LNP* Thermocomp* RX96592 is a compound based on Nylon 6/6 containing Proprietary Fillers. |
|||
Flexural Modulus | 9.14 GPa | 1330 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp PF007 PA 6 (Asia Pacific) LNP* Thermocomp* PF007 is a compound based on Nylon 6 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |