Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon DEF13 PC LNP* Stat-kon* DEF13 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was sup.. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS LNP* THERMOCOMP* AFB42 is a compound based on ABS containing 10% Glass Fiber, 20% Glass Bead. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66 LNP* Thermocomp* RF007H is a compound based on Nylon 66 containing glass fiber. Added feature includes: Healthcare. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF007SXP PA 66 LNP* THERMOCOMP* RF007SXP is a compound based on Nylon 66 containing 35% Glass Fiber. Added feature of this material includes: Heat Stabilized. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66 LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66 (Asia Pacific) LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT LNP* THERMOCOMP* WF006H is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Modulus | 9.44 GPa | 1370 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT (Asia Pacific) LNP* Thermocomp* WF006H is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |