Polymer Property : Flexural Modulus = 943 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	6.50 GPa	943 ksi	STN EN ISO 178
Plastcom PLASTAMID® 6 GF 30 031 TS PA6 reinforced with glass fiber, heat stabilized PA 6 for injection molding, reinforced with 30% glass fiber, heat stabilized, better surface appearance of injection moldings. Decrease in tensile strength by 50 % after 5000 hours at 170°C. Used f..
Flexural Modulus	6.50 GPa	943 ksi
Plastcom SLOVALEN PH 49 GF 40 PP, 40% glass fibre PP homopolymer for injection moulding, chemically strengthened with 40% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-go..
Flexural Modulus	6.50 GPa	943 ksi
Plastcom SLOVASTER® B/A GF 20 PBT, 20% glass fibre FeaturesPBT/ASA for injection moulding, chemically reinforced with 20% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and ben..
Flexural Modulus	6.50 - 10.5 GPa	943 - 1520 ksi	Average value: 8.61 GPa Grade Count:15
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. ..
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
Gharda Chemicals Gafone S 1320GF Polysulfone (PS) (discontinued **) Characteristics: High Temperature Resistance - Tg 189°C Excellent Clarity Excellent Mechanical & Electrical properties Easy to process Very good Hydrolytic Resistance Applications: Elec..
Flexural Modulus	6.50 GPa	943 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8108 PEEK, with glass fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.Improved frict..
Flexural Modulus	6.50 GPa	943 ksi
Lehmann & Voss LUVOCOMÂ® 1/GF/20/TF/10/SI/2/BK Polyamide 66, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Bearings, ..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2200F PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be supported with b..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2200R PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. UL94 V0 and 5VA listing.
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2210 PEI (Europe-Africa-Middle East) 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing.
Flexural Modulus	6.50 GPa	943 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 4521 PBT (Europe-Africa-Middle East) VALOX 4521 is a high flow, 19.5% glass reinforced flame retardant PBT injection moulding resin. Applications: electrical applications.
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
Solvay Specialty Polymers VeradelÂ® 3320GF Polyethersulfone (PESU), 20% Glass Fiber VeradelÂ® 3320GF is a 20% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, ..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp BX06088 SAN (Europe-Africa-Middle East) LNP* THERMOCOMP* BX06088 is a compound based on Styrene Acrylonitrile Blend resin containing Carbon Fiber. Added features include: Electrically Conductive.This data was supplied by SABIC-IP for the..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RFB24 is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
Plenco 7203 Phenolic, Granular, Transfer Molded PLENCO 07203 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and an industrial finish. UL recognized under component file E40654. 07203 is available i..
Flexural Modulus	6.50 GPa	943 ksi	ASTM-D790
Polyram RamSter PF320G4 PBT, 20% Glass Fiber, Flame Retardant 20% Glass fiber reinforced, flame retardant PBT for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	6.50 GPa	943 ksi	2mm/min; ISO 178
Borealis Xmod™ GD301FE Polypropylene, Glass Fiber Reinforced Xmod™ GD301FE is a 30 % chemically coupled high performance glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also a..
Flexural Modulus	6.50 GPa	943 ksi	ASTM-D790
Polyram RamOfin PPH300G8 Polypropylene, 40% Glass Fiber 40% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	6.50 GPa	943 ksi	cond; ISO 178
DSM Novamid® 3021GH30 NAT PA66-GF30 30% Glass Reinforced, Heat Stabilized
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Ascend Performance Materials Vydyne® R533 NT Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533 NT is general-purpose, 33% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade that is lubricated for good machine feed, flow and mold release. Gl..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Ascend Performance Materials Vydyne® R533H01 Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533H01 is 33% glass-fiber reinforced, hydrolysis-resistant, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties whe..
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
A. Schulman ComAlloy Hiloy® 622 Nylon 6/6, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Modulus	6.50 GPa	943 ksi	2 [mm/min]; ISO 178
Akro-Plastic Akromid® S3 GF 23 1 (2917) PA 6.10 Dry, 23% Glass Filled A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
BASF Ultramid® A3WG6 BK 00564 30% Glass Filled PA66 (Conditioned) Description: 30% glass-fiber reinforced and heat aging resistant injection-molding grade for machine elements and housings of high stiffness and dimensional stability such as lamp socket housings, f..
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
Beijing Ranger Chem PBT-201-G10 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Modulus	6.50 GPa	943 ksi	cond; ISO 178
DSM Novamid® 3021GH30 BK629 PA66-GF30 30% Glass Reinforced, Heat Stabilized
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
DSM Akulon® K-FHGM24 (Dry) 30% Glass/Mineral Reinforced, Nylon 6 (North America) (discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Ascend Performance Materials Vydyne® R533H BK02 Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533H BK02 is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-f..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Ascend Performance Materials Vydyne® R533H BK0201 Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533H BK0201 is 33% glass-fiber reinforced, hydrolysis-resistant, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical propertie..
Flexural Modulus	6.50 GPa	943 ksi
Lehmann & Voss LUVOCOM® 1105-7107/BK PEEK, with glass fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio..