Polymer Property : Flexural Strength = 155 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	155 MPa @Temperature 23.0 °C	22500 psi @Temperature 73.4 °F	ISO 178
Victrex® PEEK 600G Polyetheretherketone (discontinued **) Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low viscosity, FDA food conta..
Flexural Strength	155 MPa @Strain 6.70 %	22500 psi @Strain 6.70 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 130 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified PA 6, 30% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Strength	155 MPa @Strain 4.00 %	22500 psi @Strain 4.00 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 25 F30 000000 Nylon 6, Glass Fiber Reinforced, Flame Retardant PA 6, 25% glass fibers, injection molding, flame retardantInformation provided by LANXESS.
Flexural Strength	155 MPa @Temperature 80.0 °C	22500 psi @Temperature 176 °F	Practical Use (Water Absorption 0.8%); ASTM-D790
Toyobo GLAMIDE® T-663G50A MXD66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	155 MPa @Temperature -40.0 °C	22500 psi @Temperature -40.0 °F	Practical Use (Water Absorption 1.9%); ASTM-D790
Toyobo GLAMIDE® TY-502NZ 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	155 MPa @Temperature -40.0 °C	22500 psi @Temperature -40.0 °F	ASTM D790
BASF Ultramid® 8202 L Intermediate PA6 (Conditioned) Description: Ultramid 8202 L-Intermediate is an unreinforced, low viscosity, non-lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is avai..
Flexural Strength	155 MPa @Temperature 23.0 °C	22500 psi @Temperature 73.4 °F	ISO 178
Victrex® PEEK 650G Polyetheretherketone Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low viscosity, FDA food conta..