Polymer Property : Flexural Strength = 207 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	207 MPa @Temperature 260 °C	30000 psi @Temperature 500 °F	Dry; ASTM D790
Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac..
Flexural Strength	207 MPa @Temperature 260 °C	30000 psi @Temperature 500 °F	Dry, Autoclave with Post-Cure; ASTM D790
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 581 Quartz Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac..
Flexural Strength	207 MPa @Temperature 216 °C	30000 psi @Temperature 420 °F	Dry, Autoclave; ASTM D790
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac..
Flexural Strength	207 MPa @Thickness 8.00 mm	30000 psi @Thickness 0.315 in	LW
Industrial Laminates/Norplex SP525M (WaveMax 5000) Glass Fabric Description: Non-woven substrate combined with high temperature, static dissipative epoxy resin. Superior machining properties. Capable of producing thin walls with high strength for finely machined..