Polymer Property : Flexural Strength = 34000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	234 MPa @Temperature 93.3 °C	34000 psi @Temperature 200 °F	Dry; ASTM D790
Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 581 Quartz Reinforced Nelcote® V-341 is Polybutadiene resin system designed to provide excellent electrical properties in demanding airborne, shipboard, and undersea applications.Key Features and Benefits:Extremely low ..
Flexural Strength	234 MPa @Thickness 1.57 mm	34000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP193M Synthetic Fabric Base Grade Description: 17 oz. aramide and â€œsoft glassâ€ fibers are combined to make a fabric that is stronger than pure aramide and less abrasive than glass fabrics. This material is impregnated with..
Flexural Strength	234 MPa @Thickness 1.57 mm	34000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP504 Glass Fabric Description: Woven glass fabric with high temperature phenolic resin. Good flexural, compressive and impact strengths at elevated temperatures. Capable of continuous operation at 175Â° C, see note..
Flexural Strength	234 MPa @Thickness 1.57 mm	34000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP610 Paper Base Laminate Description: Phenolic paper based grade for mechanical applications. Good tensile, compressive and flexural strength. Primarily a machining material, but may be hot punched up to .093" thick.Thickne..
Flexural Strength	234 MPa @Thickness 1.57 mm	34000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP613 Paper Base Laminate Description: NP613 is constructed from electrical grade of kraft paper and a specially modified epoxy resin system. It is designed to be used in tap changers, coil support plates and terminal panels..