Mechanical Properties	Metric	English	Comments
Shear Strength	13.1 MPa @Temperature 204 Â°C	1900 psi @Temperature 400 Â°F	ASTM D732
Greene Tweed AvalonÂ® 1 PTFE Products made from AvalonÂ® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin..
Shear Strength	13.1 MPa @Temperature 93.3 °C	1900 psi @Temperature 200 °F	Lap Shear
Hexcel® Redux® 335K Adhesive film for bonding metallic and composite components (0.06 psf) Redux 335 is a film adhesive curing at 250F. It is available in a range of standard areal weights from 0.015 to 0.06 psf. It is available either unsupported or with knitted and/or matt carrier for a..
Shear Strength	13.1 MPa @Temperature 82.0 °C	1900 psi @Temperature 180 °F	with Scotch-Weld EW-5000; ASTM D1002-10
3M Scotch-Weld™ EC-2815 B/A FR Epoxy Adhesive 3M Scotch-Weld Epoxy Adhesive EC-2815 B/A FR is a two-component epoxy adhesive with cure at room temperature or with additional heat to form a tough, impact-resistant bond. It has excellent adhesion..
Shear Strength	13.1 MPa @Time 86400 sec	1900 psi @Time 24.0 hour	Overlap, PVC
3M Scotch-Weld™ EZ250030 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds a wide variety of plastics and wood to th..
Shear Strength	13.1 MPa @Temperature 23.0 °C	1900 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
3M Scotch-Weld™ TE100 Black Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..