3M Scotch-Weld™ TE100 Black Polyurethane Reactive Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ TE100 Black Polyurethane Reactive Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Extrudable grade adhesive with medium set time and low viscosity ideal for bonding wood. Bonds selected plastics. Yields thin glue lines.Information provided by 3M
Physical Properties Metric English Comments
Density >= 1.05 g/cc
>= 0.0379 lb/in³
Brookfield Viscosity 9000 cP
9000 cP
Thermosel using spindle #27
Mechanical Properties Metric English Comments
Hardness, Shore D 57
57
Tensile Strength at Break 26.5 MPa
3840 psi
ASTM D638 Die C
Elongation at Break 675 %
675 %
ASTM D638 Die C
Tensile Modulus 0.0517 GPa
7.50 ksi
ASMT D638 Die C
Shear Strength 3.79 MPa

@Temperature 82.0 °C
550 psi

@Temperature 180 °F
Overlap, Maple
4.90 MPa

@Temperature 23.0 °C
710 psi

@Temperature 73.4 °F
Overlap, Polystyrene, Substrate Failure
6.83 MPa

@Temperature 23.0 °C
990 psi

@Temperature 73.4 °F
Overlap, ABS
7.93 MPa

@Temperature 82.0 °C
1150 psi

@Temperature 180 °F
Overlap, FRP
9.17 MPa

@Temperature 23.0 °C
1330 psi

@Temperature 73.4 °F
Overlap, Polyacrylic, Substrate Failure
11.9 MPa

@Temperature 23.0 °C
1720 psi

@Temperature 73.4 °F
Overlap, Polycarbonate
13.1 MPa

@Temperature 23.0 °C
1900 psi

@Temperature 73.4 °F
Overlap, PVC, Substrate Failure
14.5 MPa

@Temperature 23.0 °C
2100 psi

@Temperature 73.4 °F
Overlap, Maple
21.8 MPa

@Temperature 23.0 °C
3160 psi

@Temperature 73.4 °F
Overlap, FRP
Peel Strength 0.175 kN/m
1.00 pli
180°, Aluminum
0.175 kN/m
1.00 pli
180°, Glass
1.93 kN/m
11.0 pli
180°, Polystyrene
11.4 kN/m
65.0 pli
180°, ABS, Cotton duck failed during testing
13.7 kN/m
78.0 pli
180°, PVC, Cotton duck failed during testing
14.0 kN/m
80.0 pli
180°, FRP, Cotton duck failed during testing
14.0 kN/m
80.0 pli
180°, Polyacrylic, Cotton duck failed during testing
17.7 kN/m
101 pli
180°, Polycarbonate, Cotton duck failed during testing
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Processing Properties Metric English Comments
Cure Time 1.00 min
0.0167 hour
Set Time
Descriptive Properties Value Comments
Appearance Black