Polymer Property : Shear Strength = 3.65 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	3.65 MPa @Temperature -55.0 °C	530 psi @Temperature -67.0 °F	Beam Shear, No conditioning
Hexcel® Redux® 330K Epoxy film adhesives for the bonding and finishing of composites Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike appl..
Shear Strength	3.65 MPa @Temperature 21.1 °C	530 psi @Temperature 70.0 °F	Beam Shear, No conditioning
Hexcel® Redux® 330K Epoxy film adhesives for the bonding and finishing of composites Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike appl..
Shear Strength	3.65 MPa @Temperature 71.1 °C	530 psi @Temperature 160 °F	Beam Shear, No conditioning
Hexcel® Redux® 330K Epoxy film adhesives for the bonding and finishing of composites Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike appl..
Shear Strength	3.65 MPa @Time 3600 sec	530 psi @Time 1.00 hour	Overlap, PVC
3M Scotch-Weld™ EZ250150 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds a wide variety of plastics and wood to th..
Shear Strength	3.65 MPa @Temperature 24.0 °C	530 psi @Temperature 75.2 °F	Overlap, Polystyrene
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	3.65 MPa @Temperature 24.0 °C	530 psi @Temperature 75.2 °F	Overlap, Polystyrene
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	3.65 MPa @Temperature 24.0 °C	530 psi @Temperature 75.2 °F	Overlap, Polystyrene
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..