3M Scotch-Weld™ EZ250150 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ EZ250150 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds a wide variety of plastics and wood to themselves and to metal glass. Long open and set time ideal for bonding a wide variety of substrates including wood, plastics and also bonds aluminum glass to plastics and wood.Information provided by 3M
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
Brookfield Viscosity 9000 cP
9000 cP
Thermosel using spindle #27
Mechanical Properties Metric English Comments
Hardness, Shore D 45
45
Tensile Strength at Break 22.8 MPa
3310 psi
ASTM D638 Die C
Elongation at Break 700 %
700 %
ASTM D638 Die C
Shear Strength 1.90 MPa

@Temperature 82.0 °C
275 psi

@Temperature 180 °F
Overlap, PVC
2.83 MPa

@Temperature 82.0 °C
410 psi

@Temperature 180 °F
Overlap, Maple
6.41 MPa

@Temperature 23.0 °C
930 psi

@Temperature 73.4 °F
Overlap, ABS, Substrate Failure
8.83 MPa

@Temperature 23.0 °C
1280 psi

@Temperature 73.4 °F
Overlap, Polyacrylic, Substrate Failure
10.3 MPa

@Temperature 23.0 °C
1490 psi

@Temperature 73.4 °F
Overlap, Polycarbonate
10.8 MPa

@Temperature 23.0 °C
1570 psi

@Temperature 73.4 °F
Overlap, Maple
11.55 MPa

@Temperature 23.0 °C
1675 psi

@Temperature 73.4 °F
Overlap, PVC
1.97 MPa

@Time Error in fixSigDigits: @digits must be between 1 a sec
285 psi

@Time Error in fixSigDigits: @digits must be between 1 a hour
Overlap, PVC
2.83 MPa

@Time Error in fixSigDigits: @digits must be between 1 a sec
410 psi

@Time Error in fixSigDigits: @digits must be between 1 a hour
Overlap, Maple
3.65 MPa

@Time 3600 sec
530 psi

@Time 1.00 hour
Overlap, PVC
5.62 MPa

@Time 3600 sec
815 psi

@Time 1.00 hour
Overlap, Maple
7.93 MPa

@Time 605000 sec
1150 psi

@Time 168 hour
Overlap, Maple
8.791 MPa

@Time 259000 sec
1275 psi

@Time 72.0 hour
Overlap, Maple
8.83 MPa

@Time 86400 sec
1280 psi

@Time 24.0 hour
Overlap, Maple
10.1 MPa

@Time 86400 sec
1460 psi

@Time 24.0 hour
Overlap, PVC
10.5 MPa

@Time 259000 sec
1530 psi

@Time 72.0 hour
Overlap, PVC
11.55 MPa

@Time 605000 sec
1675 psi

@Time 168 hour
Overlap, PVC
Peel Strength 8.77 kN/m
50.0 pli
180°, Polyacrylic
8.77 kN/m
50.0 pli
180°, Aluminum
9.64 kN/m
55.0 pli
180°, ABS
10.5 kN/m
60.0 pli
180°, Glass
13.1 kN/m
75.0 pli
180°, PVC, Cotton duck failed during testing
16.7 kN/m
95.0 pli
180°, Polycarbonate, Cotton duck failed during testing
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Processing Properties Metric English Comments
Cure Time 2.50 min
0.0417 hour
Set Time
Descriptive Properties Value Comments
Appearance white/off-white