Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 30.0 MPa @Temperature 24.0 °C |
4350 psi @Temperature 75.2 °F |
Short Beam |
Hexcel® F161 Epoxy Resin, 285 Kevlar Fabric Hexcel designation: 285-38"-F161; Fiber: Kev. 49 1140Information provided by HexCel |
|||
Shear Strength | 30.0 MPa @Temperature 24.0 °C |
4350 psi @Temperature 75.2 °F |
Short Beam |
Hexcel® F161 Epoxy Resin, 285 Kevlar Fabric Hexcel designation: 285-38"-F161; Fiber: Kev. 49 1140Information provided by HexCel |
|||
Shear Strength | 30.0 MPa @Temperature 22.2 °C |
4350 psi @Temperature 72.0 °F |
Lap Shear |
Hexcel® Redux® 610W (0.03 psf) Flame retarded epoxy film adhesive Redux 610 is a modified, flame-retarded epoxy film adhesive curing at 250°F. It is suitable for bonding metal to metal and for sandwich structures where flame retardancy and low heat release are re.. |
|||
Shear Strength | 30.0 MPa @Temperature 22.2 °C |
4350 psi @Temperature 72.0 °F |
Lap Shear |
Hexcel® Redux® 610W (0.06 psf) Flame retarded epoxy film adhesive Redux 610 is a modified, flame-retarded epoxy film adhesive curing at 250°F. It is suitable for bonding metal to metal and for sandwich structures where flame retardancy and low heat release are re.. |
|||
Shear Strength | 30.0 MPa @Temperature 127 °C |
4350 psi @Temperature 260 °F |
Lap Shear |
Hexcel® Redux® 641K Modified epoxy film adhesive for bonding metallic and composite components Redux 641 is a high temperature modified epoxy film adhesive curing at 350°F. It is suitable for bonding metal to metal and for sandwich structures where operating temperatures are experienced up t.. |