Polymer Property : Shear Strength = 44.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	44.0 MPa @Temperature 140 °C	6380 psi @Temperature 284 °F	ILSS; prEN2563
Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/G1089/1000 Fabric Fiber: T800H 6K 2x2 Twill, 200 g/m2Information provided by HexCel
Shear Strength	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in Skydrol 500A at 72°F
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve..
Shear Strength	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Unprimed, No conditioning of Redux 319
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve..
Shear Strength	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in synthetic esters at 72°F
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve..
Shear Strength	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in synthetic esters at 72°F
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve..
Shear Strength	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in anti-icing fluid at 72°F
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve..
Shear Strength	44.0 MPa @Temperature 60.0 °C	6380 psi @Temperature 140 °F	0º Interlaminar Shear, Conditioning: 60°C-90%RH; ASTM D2344
Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg IM2-C Fibre 1947 - 38% resin weight with IM2-C 53% fiber volumeInformation provided by HexCel
Shear Strength	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear
Hexcel® Redux® 641K Modified epoxy film adhesive for bonding metallic and composite components Redux 641 is a high temperature modified epoxy film adhesive curing at 350°F. It is suitable for bonding metal to metal and for sandwich structures where operating temperatures are experienced up t..
Shear Strength	44.0 MPa @Temperature -55.0 °C	6380 psi @Temperature -67.0 °F	Adhered: 50 MIL (6-4 Titanium Alloy), Adhesive AF-126 (0.06 wt)
3M Scotch-Weld™ 3901 Metal Primer 3M™ Scotch-Weld™ Metal Primer 3901 is a primer for 3M™ Scotch-Weld™ film and liquid adhesives in those applications where it is desired to obtain improved metal and glass adhesion or improved re..