Polymer Property : Shear Strength = 5400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	37.2 MPa @Temperature 93.3 °C	5400 psi @Temperature 200 °F	Short-Beam, Dry; ASTM D2344
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Shear Strength	37.2 MPa @Temperature 21.1 °C	5400 psi @Temperature 70.0 °F	Short-Beam, Wet; ASTM D2344
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Shear Strength	37.2 MPa @Temperature 175 °C	5400 psi @Temperature 347 °F	Laminate property; In Line Shear; Conditioning: 158°F 85% RH sat
Hexcel® HexFlow® RTM651 One-part Modified BMI Resin HexFlow® RTM651 is a one-component modified bismaleimide for resin transfer molding (RTM). Upon heating to 212-248°F, the resin will become a low viscosity homogeneous liquid that has a long pot-l..
Shear Strength	37.2 MPa @Temperature 163 °C	5400 psi @Temperature 325 °F	Short Beam, Wet (Immersed in water at 71°C for 7 days)
Hexcel® HexPly® 954-2A Curing Cyanate Resin, Quartz Fiber Reinforced 8 Harness Satin Fabric Information provided by HexCel
Shear Strength	37.2 MPa @Temperature 204 °C	5400 psi @Temperature 399 °F	Short Beam
Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric Information provided by HexCel
Shear Strength	37.2 MPa @Temperature 149 °C	5400 psi @Temperature 300 °F	Short Beam, Wet
Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric Information provided by HexCel
Shear Strength	37.2 MPa @Temperature 21.1 °C	5400 psi @Temperature 70.0 °F	Lap Shear
Hexcel® Redux® 312 Modified epoxy film adhesive (0.015 psf) Redux® 312 is a high-strength 250°F curing film adhesive, suitable for metal to metal bonding and sandwich constructions, where operating temperatures of up to 210°F may be experienced. A support..
Shear Strength	37.2 MPa @Temperature 21.1 °C	5400 psi @Temperature 70.0 °F	Single Lap Shear (Metal/Metal), 0.03 psf, No conditioning
Hexcel® Redux® 330M Epoxy film adhesives for the bonding and finishing of composites Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike appl..
Shear Strength	37.2 MPa @Temperature 21.1 °C	5400 psi @Temperature 70.0 °F	Tensile Shear, Redux 775 film
Hexcel® Redux® 775 Vinyl phenolic structural adhesive Redux 775 was adopted as the world's first metal-to-metal bonding process to be officially approved for use in the manufacture of aircraft primary structures in 1943. It is available either as a fil..