Hexcel® HexPly® 954-2A Curing Cyanate Resin, Quartz Fiber Reinforced 8 Harness Satin Fabric

Category Polymer , Thermoset , Epoxy
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® 954-2A Curing Cyanate Resin, Quartz Fiber Reinforced 8 Harness Satin Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 648 MPa
<br>@Temperature 23.0 °C
 94000 psi
<br>@Temperature 73.4 °F
 0°
Elongation at Yield 3.5 %
<br>@Temperature 23.0 °C
 3.5 %
<br>@Temperature 73.4 °F
Tensile Modulus 22.1 GPa
<br>@Temperature 23.0 °C
 3210 ksi
<br>@Temperature 73.4 °F
 0°
Flexural Yield Strength 765 MPa
<br>@Temperature 23.0 °C
 111000 psi
<br>@Temperature 73.4 °F
Flexural Modulus 20.7 GPa
<br>@Temperature 23.0 °C
 3000 ksi
<br>@Temperature 73.4 °F
Compressive Yield Strength 345 MPa
<br>@Temperature 163 °C
 50000 psi
<br>@Temperature 325 °F
 0°, Wet (Immersed in water at 71°C for 7 days)
359 MPa
<br>@Temperature 149 °C
 52100 psi
<br>@Temperature 300 °F
 0°, Wet (Immersed in water at 71°C for 7 days)
372 MPa
<br>@Temperature 177 °C
 54000 psi
<br>@Temperature 351 °F
 0°
407 MPa
<br>@Temperature 163 °C
 59000 psi
<br>@Temperature 325 °F
 0°
517 MPa
<br>@Temperature 23.0 °C
 75000 psi
<br>@Temperature 73.4 °F
Compressive Modulus 21.4 GPa
<br>@Temperature 177 °C
 3100 ksi
<br>@Temperature 351 °F
 0°
23.4 GPa
<br>@Temperature 163 °C
 3390 ksi
<br>@Temperature 325 °F
 0°
23.4 GPa
<br>@Temperature 149 °C
 3390 ksi
<br>@Temperature 300 °F
 0°, Wet (Immersed in water at 71°C for 7 days)
23.4 GPa
<br>@Temperature 163 °C
 3390 ksi
<br>@Temperature 325 °F
 0°, Wet (Immersed in water at 71°C for 7 days)
23.4 GPa
<br>@Temperature 23.0 °C
 3390 ksi
<br>@Temperature 73.4 °F
Shear Strength 37.2 MPa
<br>@Temperature 163 °C
 5400 psi
<br>@Temperature 325 °F
 Short Beam, Wet (Immersed in water at 71°C for 7 days)
44.1 MPa
<br>@Temperature 149 °C
 6400 psi
<br>@Temperature 300 °F
 Short Beam, Wet (Immersed in water at 71°C for 7 days)
44.8 MPa
<br>@Temperature 177 °C
 6500 psi
<br>@Temperature 351 °F
 Short Beam
46.2 MPa
<br>@Temperature 163 °C
 6700 psi
<br>@Temperature 325 °F
 Short Beam
71.7 MPa
<br>@Temperature 23.0 °C
 10400 psi
<br>@Temperature 73.4 °F
Electrical Properties Metric English Comments
Dielectric Constant 3.22
<br>@Frequency 2.07e+10 Hz,<br> Temperature 23.0 °C
 3.22
<br>@Frequency 2.07e+10 Hz,<br> Temperature 73.4 °F
 Ambient moisture content
3.32
<br>@Frequency 4.45e+10 Hz,<br> Temperature 23.0 °C
 3.32
<br>@Frequency 4.45e+10 Hz,<br> Temperature 73.4 °F
 Ambient moisture content
Dielectric Loss Index 0.0060
<br>@Frequency 2.07e+10 Hz,<br> Temperature 23.0 °C
 0.0060
<br>@Frequency 2.07e+10 Hz,<br> Temperature 73.4 °F
 Ambient moisture content
0.0060
<br>@Frequency 4.45e+10 Hz,<br> Temperature 23.0 °C
 0.0060
<br>@Frequency 4.45e+10 Hz,<br> Temperature 73.4 °F
 Ambient moisture content