Polymer Property : Glass Transition Temp, Tg = 169 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 76.1 - 170 °C
169 - 338 °F
Average value: 107 °C Grade Count:7
Overview of materials for Epoxy/Carbon Fiber Composite
This property data is a summary of similar materials in the MatWeb database for the category "Epoxy/Carbon Fiber Composite". Each property range of values reported is minimum and maximum values of a..
Glass Transition Temp, Tg 76.1 °C
169 °F
Neat Resin; After 24 hr water boil
Fibre Glast 3100 Style 7781 Prepreg E-Glass Fiberglass Fabric
Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts ..
Glass Transition Temp, Tg 76.1 °C
169 °F
Neat Resin; After 24 hr water boil
Fibre Glast 3101 3K, 2x2 Twill Weave Prepreg Carbon Fiber Fabric
Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts ..
Glass Transition Temp, Tg 76.1 °C
169 °F
Neat Resin; After 24 hr water boil
Fibre Glast 3102 2x2 Twill Weave Prepreg Kevlar Fabric
Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts ..
Glass Transition Temp, Tg 76.0 °C
169 °F
Lucite International Elvacite ® 2013 Acrylic Resin
Elvacite® 2013 is a low molecular weight methyl methacrylate / n-butyl methacrylate copolymer. It is a fast – dissolving, low viscosity grade with quick solvent release for use in industrial..
Glass Transition Temp, Tg 76.0 °C
169 °F
Lucite International Elvacite ® 4402 Acrylic Resin
Elvacite® 4402 is a solid methyl methacrylate copolymer bead resin designed for use in formulating environmentally sound thermosetting coatings and adhesives. The resin may be used as the main b..
Glass Transition Temp, Tg 76.0 °C
169 °F
Ultimate Tg
Tra-Con Tra-Cast 3108 General Purpose Epoxy Casting Compound
TRA-CAST 3108 is a low viscosity two-part formulation recommended for underfill and encapsulating applications where the combination of good mechanical thermal and electrical properties are required..
Glass Transition Temp, Tg 76.0 - 94.0 °C
169 - 201 °F
ASTM E1545-00
DSM Somos® ProtoGen™ O-XT 18120 Epoxy Resin for Stereolithography, UV & Thermal Postcure
DescriptionDSM Somos® ProtoGen O-XT 18120 is a liquid photopolymer that produces accurate parts ideal for general purpose applications. ProtoGen resins are the first SL resins to demonstrate diffe..
Glass Transition Temp, Tg 76.0 °C
169 °F
DayGlo Gem-Tone GC-13P Ruby Red
Gem-Tone® GC-13P Ruby Red is a rich, strong blue shade red colorant intended for use in clarified polypropylene. Clean, haze free, non-warping color formulations can easily be achieved with the use..
Glass Transition Temp, Tg 76.0 °C
169 °F
90 Minute UV Cure; DMA, E"
3D Systems Accura® SI 40 Plastic for the SLA® 250 System
Accura 40 "Ar" or "Hc" type materials - for the SLA 250 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing ..
Glass Transition Temp, Tg 76.0 °C
169 °F
ISO 11357-1,-2,-3
Celanese IMPET 830R PET, 35% Mineral / Glass Reinforced
Impet 830R is a 35% glass/mineral reinforced injection moldable polyester made with recycled PET. It provides an excellent combination of strength, stiffness, warp resistance, and high temperature c..
Glass Transition Temp, Tg 75.9 °C
169 °F
90 Minute UV Cure; DMA, E"
3D Systems Accura® SI 40 Plastic for the SLA® 500 System
Accura 40 "Ar" or "Hc" type materials - for the SLA 500 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing ..
Copyright © lookpolymers.com All Rights Reserved