Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 137 Â°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	137 Â°C @Thickness 4.00 mm	279 Â°F @Thickness 0.157 in	Annealed; ASTM D648
LG Chemical Lupoy 1621-02 Polycarbonate Resin Description: LUPOY PC 1621-02 resin is designed for large injection stretch blow molding and extrusion blow molding parts. It exhibits an excellent physical property balance of heat resistance, tran..
Deflection Temperature at 1.8 MPa (264 psi)	137 Â°C @Thickness 3.20 mm	279 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics NORYL RN1300 PPE (Asia Pacific) 15% glass/mineral reinforced PPE. Nonchlorinated, nonbrominated, flame-retardant. Black and gray.
Deflection Temperature at 1.8 MPa (264 psi)	137 Â°C @Thickness 3.20 mm	279 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC LNP* Stat-kon* Lexan_LC1500N compound is a 15% carbon fiber, 6% PTFE reinforced polycarbonate.
Deflection Temperature at 1.8 MPa (264 psi)	137 Â°C @Thickness 3.20 mm	279 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East) LNP* Stat-kon* Lexan_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate.
Deflection Temperature at 1.8 MPa (264 psi)	137 °C @Thickness 3.20 mm	279 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific) 15% carbon fiber, 6% PTFE reinforced polycarbonate.