- Polymer Property : CTE, linear = 14.8 µm/m-°C
Polymer Property : CTE, linear = 14.8 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.20 µin/in-°F @Temperature 69.8 - 601 °F |
|
| H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy MP35N is a nickel-cobalt based alloy of the Multiphase® alloy system that has ultra high strength, toughness, ductility, biocompatibility, and outstanding corrosion resistance. H.C. Starck offers.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 20.0 - 900 °C |
8.22 µin/in-°F @Temperature 68.0 - 1650 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 760 °C |
8.22 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 26.0 - 538 °C |
8.22 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 26.0 - 538 °C |
8.22 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 26.0 - 538 °C |
8.22 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 26.0 - 538 °C |
8.22 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature -25.0 °C |
8.22 µin/in-°F @Temperature -13.0 °F |
|
| CRP Technology AMC225xe Aluminum Alloy - SiC Composite, T4 Condition AMC225xe is a high quality aerospace grade aluminum alloy (AA2124) reinforced with 25% by volume of ultrafine particles of silicon carbide. It is manufactured by a special powder metallurgy route us.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 20.0 - 299 °C |
8.20 µin/in-°F @Temperature 68.0 - 570 °F |
|
| Carlson 2205 (UNS S31803) Duplex Stainless Steel General DescriptionCarlson Alloy 2205 is a second-generation, nitrogen-alloyed duplex stainless steel (ferritic-austenitic). It offers an excellent combination of both strength and corrosion resist.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction + Aged 538°C (1000°F)/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 55% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 760 °C |
8.22 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||