H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy

Category Metal , Nonferrous Metal , Cobalt Alloy , Nickel Alloy , Superalloy
Manufacturer H.C. Starck
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MP35N is a nickel-cobalt based alloy of the Multiphase® alloy system that has ultra high strength, toughness, ductility, biocompatibility, and outstanding corrosion resistance. H.C. Starck offers MP35N alloy in flat rolled plate, sheet, and foil products. MP35N is produced by vacuum induction melting and consumable vacuum arc re-melting. Strengthened by work hardening and aging to levels of 260 to 300 ksi (1790 to 2070 MPa), MP35N has good ductility with greater than 40% reduction in area, and good toughness. MP35N can be effectively utilized at cryogenic temperatures without embrittlement and up to 600°F without loss in performance. The high strength and corrosion resistance, high modulus, ease of fabrication, and other mechanical properties make MP35N an ideal candidate for high performance products, where emphasis is placed upon dependability for demanding applications.MP35N products are used in diverse applications:Biomedical uses: Orthodontics and ProstheticsOil Industry, Chemical and Marine equipment – Valve components, springs, high pressure door dogsAircraft and Aerospace components – Springs, leading edge stripsHigh Pulse Magnet ResearchInformation provided by H.C. Starck.
Physical Properties Metric English Comments
Density 8.43 g/cc
0.305 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 7.0
7.0
Annealed
44
44
50% Cold Rolled
47
47
50% Cold Rolled (4 hrs at 1025°F/550°C)
Hardness, Vickers 220
220
Annealed
420
420
50% Cold Rolled
480
480
50% Cold Rolled (4 hrs at 1025°F/550°C)
Tensile Strength, Ultimate 758 MPa
110000 psi
Annealed
1520 MPa
220000 psi
50% Cold Rolled
1830 MPa
265000 psi
50% Cold Rolled (4 hrs at 1025°F/550°C)
Tensile Strength, Yield 345 MPa
50000 psi
Annealed
1380 MPa
200000 psi
50% Cold Rolled
1550 MPa
225000 psi
50% Cold Rolled (4 hrs at 1025°F/550°C)
Elongation at Break 3.0 %
3.0 %
50% Cold Rolled (4 hrs at 1025°F/550°C)
10 %
10 %
50% Cold Rolled
60 %
60 %
Annealed
Modulus of Elasticity 201 GPa

@Temperature 482 °C
29200 ksi

@Temperature 900 °F
Annealed
201 GPa

@Temperature 482 °C
29200 ksi

@Temperature 900 °F
Cold Worked
216 GPa

@Temperature 232 °C
31300 ksi

@Temperature 450 °F
Annealed
219 GPa

@Temperature 232 °C
31800 ksi

@Temperature 450 °F
Cold Worked
233 GPa

@Temperature 25.6 °C
33800 ksi

@Temperature 78.1 °F
Annealed
235 GPa

@Temperature 25.6 °C
34100 ksi

@Temperature 78.1 °F
Cold Worked
Poissons Ratio 0.38

@Temperature 232 °C
0.38

@Temperature 450 °F
Calculated; Annealed
0.40

@Temperature 25.6 °C
0.40

@Temperature 78.1 °F
Calculated; Annealed
0.42

@Temperature 482 °C
0.42

@Temperature 900 °F
Calculated; Annealed
0.45

@Temperature 25.6 °C
0.45

@Temperature 78.1 °F
Calculated; Cold Worked
0.46

@Temperature 232 °C
0.46

@Temperature 450 °F
Calculated; Cold Worked
0.47

@Temperature 482 °C
0.47

@Temperature 900 °F
Calculated; Cold Worked
Shear Modulus 68.0 GPa

@Temperature 482 °C
9860 ksi

@Temperature 900 °F
Cold Worked
71.0 GPa

@Temperature 482 °C
10300 ksi

@Temperature 900 °F
Annealed
75.0 GPa

@Temperature 232 °C
10900 ksi

@Temperature 450 °F
Cold Worked
78.0 GPa

@Temperature 232 °C
11300 ksi

@Temperature 450 °F
Annealed
81.0 GPa

@Temperature 25.6 °C
11700 ksi

@Temperature 78.1 °F
Cold Worked
83.0 GPa

@Temperature 25.6 °C
12000 ksi

@Temperature 78.1 °F
Annealed
Thermal Properties Metric English Comments
CTE, linear 12.8 µm/m-°C

@Temperature 21.0 - 93.0 °C
7.10 µin/in-°F

@Temperature 69.8 - 199 °F
13.7 µm/m-°C

@Temperature 21.0 - 204 °C
7.60 µin/in-°F

@Temperature 69.8 - 399 °F
14.8 µm/m-°C

@Temperature 21.0 - 316 °C
8.20 µin/in-°F

@Temperature 69.8 - 601 °F
14.9 µm/m-°C

@Temperature 21.0 - 427 °C
8.30 µin/in-°F

@Temperature 69.8 - 801 °F
15.7 µm/m-°C

@Temperature 21.0 - 538 °C
8.70 µin/in-°F

@Temperature 69.8 - 1000 °F
Thermal Conductivity 6.48 W/m-K

@Temperature -184 °C
45.0 BTU-in/hr-ft²-°F

@Temperature -299 °F
9.08 W/m-K

@Temperature -73.0 °C
63.0 BTU-in/hr-ft²-°F

@Temperature -99.4 °F
11.2 W/m-K

@Temperature 21.0 °C
78.0 BTU-in/hr-ft²-°F

@Temperature 69.8 °F
12.7 W/m-K

@Temperature 93.0 °C
88.0 BTU-in/hr-ft²-°F

@Temperature 199 °F
15.0 W/m-K

@Temperature 204 °C
104 BTU-in/hr-ft²-°F

@Temperature 399 °F
17.0 W/m-K

@Temperature 316 °C
118 BTU-in/hr-ft²-°F

@Temperature 601 °F
19.2 W/m-K

@Temperature 427 °C
133 BTU-in/hr-ft²-°F

@Temperature 801 °F
21.3 W/m-K

@Temperature 538 °C
148 BTU-in/hr-ft²-°F

@Temperature 1000 °F
23.3 W/m-K

@Temperature 649 °C
162 BTU-in/hr-ft²-°F

@Temperature 1200 °F
Melting Point 1315 - 1440 °C
2399 - 2620 °F
Solidus 1315 °C
2399 °F
Liquidus 1440 °C
2620 °F
Component Elements Properties Metric English Comments
Chromium, Cr 20 %
20 %
Cobalt, Co 35 %
35 %
Molybdenum, Mo 10 %
10 %
Nickel, Ni 35 %
35 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000990 ohm-cm

@Temperature -184 °C
0.0000990 ohm-cm

@Temperature -299 °F
0.000101 ohm-cm

@Temperature -73.0 °C
0.000101 ohm-cm

@Temperature -99.4 °F
0.000103 ohm-cm

@Temperature 21.0 °C
0.000103 ohm-cm

@Temperature 69.8 °F
0.000105 ohm-cm

@Temperature 93.0 °C
0.000105 ohm-cm

@Temperature 199 °F
0.000108 ohm-cm

@Temperature 204 °C
0.000108 ohm-cm

@Temperature 399 °F
0.000110 ohm-cm

@Temperature 316 °C
0.000110 ohm-cm

@Temperature 601 °F
0.000113 ohm-cm

@Temperature 427 °C
0.000113 ohm-cm

@Temperature 801 °F
0.000115 ohm-cm

@Temperature 538 °C
0.000115 ohm-cm

@Temperature 1000 °F
0.000118 ohm-cm

@Temperature 649 °C
0.000118 ohm-cm

@Temperature 1200 °F
Magnetic Permeability 1.00085

@Temperature 119 °C
1.00085

@Temperature 246 °F
1.00092

@Temperature 25.0 °C
1.00092

@Temperature 77.0 °F
1.00096

@Temperature -27.0 °C
1.00096

@Temperature -16.6 °F
1.00104

@Temperature -73.0 °C
1.00104

@Temperature -99.4 °F
1.00117

@Temperature -140 °C
1.00117

@Temperature -220 °F
1.00142

@Temperature -195 °C
1.00142

@Temperature -319 °F
Magnetic Susceptibility 8.03

@Temperature 119 °C
8.03

@Temperature 246 °F
µ emu/g
8.7

@Temperature 25.0 °C
8.7

@Temperature 77.0 °F
µ emu/g
9.22

@Temperature -27.0 °C
9.22

@Temperature -16.6 °F
µ emu/g
9.81

@Temperature -73.0 °C
9.81

@Temperature -99.4 °F
µ emu/g
11.07

@Temperature -140 °C
11.07

@Temperature -220 °F
µ emu/g
13.47

@Temperature -195 °C
13.47

@Temperature -319 °F
µ emu/g